Wettability between molten slag and dolomitic refractory
Wettability between molten slag and dolomitic refractory
复制标题
熔渣与白云质耐火材料之间的润湿性
DOI：
10.1016/j.ceramint.2016.07.113
复制
发表时间：
2016-11
影响因子：
5.2
通讯作者：
Wang Qiangqiang
中科院分区：
文献类型：
--
作者：
Shen Ping;Zhang Lifeng;Wang Yi;Sridhar Seetharaman;Wang Qiangqiang
本文研究了钢包精炼过程中熔渣与钢包中的铁系耐火材料之间的润湿性。随着温度的升高，熔渣与刚玉质基体的接触角减小。碱度较低的炉渣更容易在基体上铺展，并渗透到基体中更深。随着保温时间的延长，熔渣在耐火材料中的渗透深度增加。耐火材料中的CaO溶解成炉渣，然后炉渣被CaO饱和。炉渣与基体反应生成了Ca3SiO5固体，减缓了炉渣向耐火材料中的进一步渗透。
In the current study, the wettability between molten slag and dolomitic refractory materials used in the ladle during steel refining was investigated. The contact angle between molten slag and dolomitic substrate decreased with increasing temperature. The slag with lower basicity spread on the substrate more easily and penetrated deeper into the substrate. The penetration depth of slag into the refractory increased with the extension of holding time. The CaO in the refractory dissolved into slag which was then saturated with CaO. The reaction between slag and substrate resulted in the formation of solid Ca3SiO5, which slowed down the further penetration of slag into the refractory.
登录
查看更多内容
DOI：
10.1016/s1003-6326(12)61818-4
发表时间：
2012-12-01
影响因子：
4.5
作者：
Heo, Seon-Hwa;Lee, Kyuyong;Chung, Yongsug
通讯作者：
Chung, Yongsug
DOI：
10.1007/bf01283477
发表时间：
1978-09
期刊：
Refractories
影响因子：
--
作者：
Yu. V. Sveshkov;V. Kalmykov;V. G. Borisov;O. A. Val'dman
通讯作者：
Yu. V. Sveshkov;V. Kalmykov;V. G. Borisov;O. A. Val'dman
DOI：
--
发表时间：
2002
期刊：
--
影响因子：
--
作者：
X. Zhong
通讯作者：
X. Zhong
影响因子：
11.4
作者：
Xiaocun Liu;Yanjun Li;Ning Zhang
通讯作者：
Xiaocun Liu;Yanjun Li;Ning Zhang
DOI：
10.2174/1874088x01105010009
发表时间：
2011-05
期刊：
The Open Materials Science Journal
影响因子：
--
作者：
Xiaoping Liang;Y. Jin;Yu Wang
通讯作者：
Xiaoping Liang;Y. Jin;Yu Wang