对2CsNO_3 + Al_2 O_3 + 2 TiO_2混合物在1530 K以下进行了热重和差热分析。结果表明，合成的产物为正交晶系的Cs2 Al 2 Ti 2 O 8，晶格参数aO=0.996，b 0 =0.898，Co=0.573 nm。同时进行TG/DTA以量化铯的重量损失和挥发，并监测作为温度的函数的相的发展和/或稳定性。
Thermogravimetry and differential thermal analyses were conducted on the mixture 2CsNO3+A12O3+2TiO2 up to 1530 K. The resultant phase was identified as orthorhombic Cs2Al2Ti2O8 with lattice parameters aO=0.996, b0=0.898, and co=0.573 nm. Simultaneous TG/DTA was performed to quantify weight loss and volatilization of cesium and to monitor the development and/or stability of the phase as a function of temperature.