Hydroxyapatite coating on Ti plate by a dipping method.
Hydroxyapatite coating on Ti plate by a dipping method.
复制标题
采用浸渍法在钛板上涂覆羟基磷灰石。
DOI：
10.3233/bme-1995-5201
复制
发表时间：
1995
影响因子：
1
通讯作者：
H. Aoki
中科院分区：
文献类型：
--
作者：
J. Lee;H. Aoki
采用浸渍法制备了羟基磷灰石(HAP)涂层金属复合材料。标本衬底为2 mm厚的钛板。采用浸渍法在HAP-Sol中进行HAP包覆1min。涂层中HAP-Sol的浓度为3.28~9.99wt%。钛基材在9.99wt%的溶胶中浸泡一次，可获得良好的涂层。经过喷砂处理的表面提供了比光滑表面好得多的涂层。随着溶胶浓度的增加，薄膜的重量发生变化，涂层厚度增加。在7wt%以上，它们的含量急剧增加。
Hydroxyapatite (HAP)-coated metal composites were made by the dipping method. The specimen substrates were Ti plates with a thickness of 2 mm. The HAP coating was carried out in HAP-sol for 1 min by the dipping method. The concentration of HAP-sol for the coating ranged from 3.28 to 9.99 wt%. Excellent coating was observed on Ti substrate dipped once in 9.99 wt% sol. A surface pretreated with a sandblasting provided a much better coating than a smooth surface. As the concentration of sol increased, the weight change and the coating thickness increased. Above 7 wt% sol, they increased sharply.