Influence of extrusion on the properties of chalcogenide glasses and fibers
Influence of extrusion on the properties of chalcogenide glasses and fibers
复制标题
挤出对硫系玻璃和纤维性能的影响
DOI：
10.1016/j.optcom.2022.128091
复制
发表时间：
2022
影响因子：
2.4
通讯作者：
Rongping Wang
中科院分区：
文献类型：
--
作者：
Junkai Sheng;Qianqian Peng;Weilu Sun;Yuze Wang;Keyu Yang;Zan Feng;Jinjing Wang;Guolin Wu;Jun Wang;Kai Jiao;Xiange Wang;Zheming Zhao;Shengchuang Bai;Xunsi Wang;Shixun Dai;Qiuhua Nie;Rongping Wang
通过测量和分析ge10as22se68和As2S3的结构和物理性能，系统地研究了挤压对硫系玻璃和纤维性能的影响。实验结果表明，挤压工艺对玻璃的网络、结晶和成分影响不大，但对玻璃的透射率、折射率和密度有影响。同时，挤压加工后的纤维损失率大大提高，分别为57.65%和71.43%，分别对应于ge10as22se68和As2S3fiber。
The influence of extrusion on the properties of chalcogenide glasses and fibers was investigated systematically via measuring and analyzing their structural and physical properties of Ge10As22Se68and As2S3. The experimental results showed that the extrusion processing has an insignificant effect on the glass network, crystallization, and compositions, but does have an influence on the glass transmission rate, refractive index and density. Meanwhile, the fiber loss after extrusion processing was greatly improved with 57.65% or 71.43%, corresponding to Ge10As22Se68or As2S3fiber, respectively.