Corrosion Behavior of FeB-30 wt.% Al0.25FeNiCoCr Cermet Coating in Liquid Zinc
Corrosion Behavior of FeB-30 wt.% Al0.25FeNiCoCr Cermet Coating in Liquid Zinc
复制标题
腐蚀%20行为%20of%20FeB-30%20wt.%%20Al0.25FeNiCoCr%20金属陶瓷%20涂层%20in%20液体%20锌
DOI：
10.3390/coatings11060622
复制
发表时间：
2021-05
期刊：
影响因子：
3.4
通讯作者：
Xuemei Ouyang
中科院分区：
文献类型：
--
作者：
Xiaolong Xie;Bingbing Yin;Fucheng Yin;Xuemei Ouyang
The corrosion of galvanizing equipment parts by liquid zinc is an urgent problem that needs solving. In this work, FeB-30 wt.% Al0.25FeNiCoCr cermet coating was deposited on the surface of 316L stainless steel by AC-HVAF to protect galvanizing equipment parts from corrosion by liquid zinc. The microstructures and phase compositions of powders and the coating were determined by SEM, EDS, and XRD in detail. Additionally, the microhardness, fracture toughness, abrasion wear resistance, and corrosion resistance of the coating to liquid zinc were also studied. The results indicate that the abrasion wear resistance and corrosion resistance of the coating are much better than that of the 316L stainless steel substrate. The failure of the coating in liquid zinc is mainly due to the penetration of liquid zinc into macro-cracks, which causes the coating to peel off.
登录
查看更多内容
DOI：
10.1007/s11661-005-0325-7
发表时间：
2005-08-01
影响因子：
2.8
作者：
Liu, XB;Barbero, E;Sikka, V
通讯作者：
Sikka, V
钼对铸态Fe-B合金组织及锌液耐蚀性能的影响
影响因子：
1.6
作者：
Ouyang, Xuemei;Chen, Guopeng;Zhao, Manxiu
通讯作者：
Zhao, Manxiu
DOI：
--
发表时间：
2013
期刊：
--
影响因子：
--
作者：
Saurabh A. Bobde;S. Kshirsagar
通讯作者：
Saurabh A. Bobde;S. Kshirsagar
影响因子：
1.8
作者：
T. Tomita;Yasuyuki Tatatani;Y. Kobayashi;Y. Harada;H. Nakahira
通讯作者：
T. Tomita;Yasuyuki Tatatani;Y. Kobayashi;Y. Harada;H. Nakahira
影响因子：
5.4
作者：
Karaoglanli, Abdullah Cahit;Oge, Mecit;Hotamis, Mert
通讯作者：
Hotamis, Mert