Research Initiation: A Three-Dimensional Mixed Finite Element Method to Integrate the Dynamic Crack Growth and Failure Mechanisms in a Composite Laminate

研究启动：三维混合有限元方法集成复合材料层合板中的动态裂纹扩展和失效机制

• 批准号: 8808241
• 负责人: Rimas Vaicaitis
• 金额: $ 6.66万
• 依托单位: Columbia University
• 依托单位国家: 美国
• 项目类别: Standard Grant
• 财政年份: 1988
• 资助国家: 美国
• 起止时间: 1988-09-01 至 1991-08-31
• 项目状态: 已结题
• 来源: https://www.nsf.gov/awardsearch/showAward?AWD_ID=8808241&HistoricalAwards=false
• 关键词: Research; Initiation; Three; Dimensional; Mixed

The objective of this research is to model the three-dimensional dynamic crack growth and failure mechanism in a composite laminate subjected to low velocity impact. This study will incorporate variationally consistent fracture mechanics elements, multi-failure criteria and parallel processing algorithms. The computational results will be checked with experimental data for low velocity impacts of an object on the surface of a composite panel and a cylinder. The resultant code will provide a quantitative design tool for predicting composite laminate failure under low velocity impact.

本研究的目的是建立三维模型， 复合材料层合板动态裂纹扩展和破坏机理 受到低速撞击。 这项研究将包括 变分一致断裂力学单元，多失效 标准和并行处理算法。 计算结果将与实验数据进行核对， 物体对复合板表面的低速撞击 和圆柱体。 由此产生的代码将提供一个定量的 用于预测复合材料层合板在低温下失效的设计工具 速度冲击