Improvement and identification of mechanical properties in forged parts by immediate post-forming after hot forging on different temperature levels by influencing microstructure of tempering steel

通过影响回火钢的显微组织，在不同温度水平下热锻后立即后成形来改善和鉴定锻件的机械性能

• 批准号: 359921546
• 负责人: Professor Dr.-Ing. Bernd-Arno Behrens
• 金额: --
• 依托单位: Institut für Umformtechnik und Umformmaschinen (IFUM)
• 依托单位国家: 德国
• 项目类别: Research Grants
• 财政年份: 2017
• 资助国家: 德国
• 起止时间: 2016-12-31 至 2020-12-31
• 项目状态: 已结题
• 来源: https://gepris.dfg.de/gepris/projekt/359921546?language=en
• 关键词: Improvement; identification; mechanical; properties; forged

In the proposed project, the microstructure of forged components should be influenced by different aspects of forging process. Furthermore these influences will be classified by evaluating typical material properties. On one hand the effect of dynamic recrystallization during the deforming process will be used to refine the microstructure, on the other hand a second deforming operation will be used to apply a thermomechanical treatment. By this combination an ultra-fine gained microstructure should be reached in the exanimated tempering steel in parts manufactured by massive forming processes. Grain refinement improves strength and toughness as well. To obtain reliable values of comparable mechanical properties of the deformed and treated material, standardized tests will be carried out. The results will be shown additionally in comprehension with results of conventionally manufactured parts.

在拟议的项目中，锻造组件的微观结构应受锻造过程的不同方面的影响。此外，这些影响将通过评估典型的材料特性进行分类。一方面，在变形过程中动态重结晶的效果将用于完善微观结构，另一方面，将使用第二个变形操作来应用热力学处理。通过这种组合，应在巨大的形成过程制造的零件中，在质量的钢钢中达到超细的微观结构。谷物精炼也可以提高力量和韧性。为了获得变形和处理过的材料的可比机械性能的可靠值，将进行标准化测试。结果将与常规制造的零件的结果相结合。

项目成果

Microstructure and Mechanical Properties of Thermomechanically Forged Tempering Steel 42CrMo4

热机械锻造回火钢42CrMo4的显微组织和力学性能

• DOI: 10.1007/978-3-662-62138-7_15
• 发表时间: 2021
• 作者: Diefenbach;Brunotte;Behrens
• 通讯作者: Behrens