Study on Correlation Between the Structure and Hydrogen Storage Properties of Palladium Nanoparticles

纳米钯颗粒结构与储氢性能相关性研究

• 批准号: 24655121
• 负责人: TERANISHI Toshiharu
• 金额: $ 2.58万
• 依托单位: Kyoto University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Challenging Exploratory Research
• 财政年份: 2012
• 资助国家: 日本
• 起止时间: 2012-04-01 至 2014-03-31
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/en/grant/KAKENHI-PROJECT-24655121/
• 关键词: ナノ粒子; コロイド; パラジウム; 結晶構造; 水素吸蔵; 結晶面; コロイド・超微粒子

Palladium (Pd) black and three kinds of single crystalline cubic Pd nanoparticles with sizes of 12, 20, and 40 nm were synthesized to investigate the size-dependent hydrogen storage/release properties of the Pd nanoparticles. A hydrogen storage capacity of Pd nanoparticles is identical to that of Pd black, although it was found that the hydrogen atoms once stored in the Pd nanoparticles are thermodynamically more stable than those in the Pd black. Both entropy and enthalpy changes of hydrides and in-situ XRD measurements support the above observation. On the other hand, the single crystalline octahedral Pd nanoparticles have the similar hydrogen storage/release properties to the Pd black.

合成了尺寸分别为12、20和40 nm的钯黑和三种单晶立方钯纳米粒子，研究了钯纳米粒子的储氢/释放性能。钯纳米粒子的储氢能力与钯黑相同，但发现在钯纳米粒子中储存的氢原子在热力学上比在钯黑中更稳定。氢化物的熵焓变化和原位XRD测量结果均支持上述观察结果。另一方面，单晶八面体钯纳米粒子具有与钯黑相似的储氢/释放特性。

项目成果

特異界面機能をもつ無機ナノ粒子

具有独特界面功能的无机纳米粒子

• 发表时间: 2013
• 作者: 佐藤良太;寺西利治 ら;Takashi Kato;寺西利治
• 通讯作者: 寺西利治

非晶質リン化パラジウムナノ粒子を媒介とした高単分散パラジウム合金ナノ粒子の新規合成法の開拓

利用非晶态磷化钯纳米颗粒开发高度单分散钯合金纳米颗粒的新合成方法

• 发表时间: 2014
• 作者: 佐藤良太;寺西利治
• 通讯作者: 寺西利治

Teranishi Laboratory

寺西研究所

プラズモンナノ材料の作り方と使い方

如何制造和使用等离子体纳米材料

• 发表时间: 2013
• 作者: 佐藤良太;寺西利治;寺西利治;寺西利治
• 通讯作者: 寺西利治

Nanoplasmonics in Inorganic Nanoparticles

无机纳米颗粒中的纳米等离子体

• 发表时间: 2012
• 作者: 佐藤良太;寺西利治;寺西利治;寺西利治;T. Teranishi
• 通讯作者: T. Teranishi