Fundamental research of the polymer dissolved ultrapure water applied to composite insulation

聚合物溶解超纯水应用于复合绝缘的基础研究

• 批准号: 25630109
• 负责人: HANAI Masahiro
• 金额: $ 2.58万
• 依托单位: Nagoya University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Challenging Exploratory Research
• 财政年份: 2013
• 资助国家: 日本
• 起止时间: 2013-04-01 至 2014-03-31
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/en/grant/KAKENHI-PROJECT-25630109/
• 关键词: 超純水; 高分子; 複合絶縁; 絶縁破壊; 比誘電率

In ultrapure water of 0.055 micro S / cm, we found that dielectric electric field is nearly constant at 14 kVrms / mm. Dielectric breakdown field of pure water was found to tend to decrease with increasing conductivity. Suppress the increase in conductivity of the water by adding (methylcellulose 25) polymer. Dielectric breakdown field of the water by adding polymer (methylcellulose 25) was substantially the same with ultrapure water. We performed the dielectric breakdown test with a composite insulating structure using a PFA coated electrode. We found that it is necessary to use a coating material having a high breakdown electric field, or it is necessary to use a relatively thick coating material.

在0.055 μ S / cm的超纯水中，我们发现介电电场在14 kVrms /mm处几乎是恒定的。纯水的介电击穿场随着电导率的增加而趋于减小。通过添加（甲基纤维素25）聚合物抑制水的电导率的增加。 通过添加聚合物（甲基纤维素25）的水的介电击穿场与超纯水基本相同。我们进行了介电击穿测试与复合绝缘结构使用PFA涂层电极。我们发现有必要使用具有高击穿电场的涂层材料，或者有必要使用相对厚的涂层材料。

项目成果

超純水の短ギャップ交流絶縁破壊特性

超纯水的短间隙交流击穿特性

• 发表时间: 2014
• 作者: 佐藤広治;小島寛樹;花井正広;加藤克巳;早川直樹
• 通讯作者: 早川直樹