Solid phase separation from molten slag

熔渣固相分离

• 批准号: 24860067
• 负责人: KUBO Hironari
• 金额: $ 1.91万
• 依托单位: Fukuoka Institute of Technology
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Research Activity Start-up
• 财政年份: 2012
• 资助国家: 日本
• 起止时间: 2012-08-31 至 2014-03-31
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/en/grant/KAKENHI-PROJECT-24860067/
• 关键词: スラグ; リン; 比重分離; 資源化; 鉄鋼製錬

The purpose of this study is to reduce the amount of steelmaking slag, especially dephosphorization slag, and to recover valuable phosphorus from the slag. When discharged, the dephosphorization slag exists as phosphorous-enriched solid phases together with matrix liquid phases containing FeO. Because of these characteristics, centrifugation experiments of molten dephosphorization slag were carried out using a centrifugal separator combined with an electric furnace. Consequently, most of the phosphorous-enriched solid phases accumulated in the upper layer of the obtained low-basicity slag.

本研究的目的是减少炼钢炉渣，特别是脱磷渣的用量，从炉渣中回收有价值的磷。排出时，脱磷渣以富磷固相形式存在，并与含FeO的基质液相共存。针对这些特点，采用离心式分离机与电炉相结合的方法对熔融脱磷渣进行了离心分离试验。因此，大部分富磷固相堆积在获得的低碱度渣的上层。

项目成果

製鋼スラグからのリン資源回収の可能性

从炼钢渣中回收磷资源的可能性

• 发表时间: 2014
• 期刊: 環境技術
• 作者: 松八重一代;久保裕也;山末英嗣;長坂徹也
• 通讯作者: 長坂徹也

溶融脱リンスラグの遠心分離

熔融洗渣的离心分离

• 发表时间: 2014
• 期刊: 福岡工業大学エレクトロニクス研究所所報
• 作者: Shuhei Yoshida;Kai Yamada;Noriyuki Unno;Jun Taniguchi;Manabu Yamamoto;赤澤真理;久保裕也
• 通讯作者: 久保裕也