Atomic scale observation of grain boundary segregation in nuclear materials by atom probe tomography and study on mechanism of grain boundary degradation

核材料晶界偏析的原子探针层析观测及晶界退化机制研究

• 批准号: 21246142
• 负责人: NAGAI Yasuyoshi
• 金额: $ 29.37万
• 依托单位: Tohoku University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (A)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/en/grant/KAKENHI-PROJECT-21246142/
• 关键词: 粒界偏析; 粒界脆化; 3次元アトムプローブ; 原子炉高経年化; 応力腐食割れ; 真空破面蒸着; レーザー; 陽電子消滅; 電子炉高経年化

It is important to understand the degradation mechanism of the grain boundary in the structural materials of aged nuclear reactors for nuclear safety. We have developed new method to observe grain boundary segregations on inter-granular fractured surfaces using laser-assisted three-dimensional atom probe method. The obtained results, combined with the other methods such as Auger electron spectroscopy and the first principles calculations, showed the relationship between inter-granular fracture and grain boundary segregations.

了解老化核反应堆结构材料中晶界的退化机理对核安全具有重要意义。我们发展了一种新的方法，用激光辅助三维原子探针方法观察晶界偏聚。结合俄歇电子能谱和第一性原理计算等方法，分析了晶界偏聚与沿晶断裂的关系。

项目成果

中性子照射された304ステンレス鋼中のNi-Si析出物の3次元アトムプローブ観察

中子辐照304不锈钢中Ni-Si析出物的3D原子探针观察

• 发表时间: 2010
• 作者: 外山健;野沢康子;永井康介;長谷川雅幸;W.van Renterghem;S.van Dyck;A.Almazouzi
• 通讯作者: A.Almazouzi

On in situ TEM analysis of crack initiation

裂纹萌生的原位 TEM 分析

• 发表时间: 2011
• 作者: 柏山祐一郎;石川可奈子;宮下英明;横山亜紀子;今村信孝;溝口正;民秋均;Y.Matsukawa
• 通讯作者: Y.Matsukawa

先進燃料被覆管材料ZrNb合金のアトムプローブ分析

先进燃料包壳材料ZrNb合金的原子探针分析

• 发表时间: 2011
• 作者: 松川義孝;齋藤健;村上有美;外山健;永井康介;金思雄;佐藤裕樹;阿部弘亨;岩井岳夫;関村直人;篠原靖周
• 通讯作者: 篠原靖周

A533B鋼粒界破面直下からの3次元アトムプローブ観察

A533B 钢晶间断裂面正下方的 3D 原子探针观察

• 发表时间: 2011
• 作者: 外山健;野沢康子;松川義孝;畠山賢彦;永井康介;西山裕孝
• 通讯作者: 西山裕孝

Time evolution of positron affinity trapping at embedded nanoparticles by age-momentum correlation

• DOI: 10.1103/physrevb.83.115459
• 发表时间: 2011-03
• 期刊: Physical Review B
• 影响因子: 3.7
• 作者: K. Inoue;Y. Nagai;Z. Tang;T. Toyama;Y. Hosoda;A. Tsuto;M. Hasegawa