Development of Severe Deformation/Non-Transformation Process Utilizing Friction Stir Processing

利用搅拌摩擦加工的严重变形/非变形工艺的开发

• 批准号: 20360334
• 负责人: FUJII Hidetoshi
• 金额: $ 12.23万
• 依托单位: Osaka University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (B)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2010
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20360334/
• 关键词: 接合; 溶接; 摩擦攪拌接合; FSW; 炭素鋼; 変態; A_1点; 接合速度; 回転速度; 高靭性; 高靱性

Friction stir welding was performed for carbon steel with different carbon contents including hyper eutectoid steel below and above the A_1 point (eutectoid temperature 723℃). The microstructures of the above A_1 joints mainly consist of martensite for higher carbon steels. Therefore, the tensile tests results are scattered. On the other hand, the microstructures of the below A_1 joints consist of a ferrite with globular cementite. The absorbed energy for the small Charpy impact test is increased for the below A_1 joints by three times.

对A_1点(共析温度723℃)以下和以上的过共析钢等不同含碳量的碳钢进行了搅拌摩擦焊。对于高碳钢，上述A_1接头的显微组织主要由马氏体组成。因此，拉伸试验结果是分散的。A_1以下接头的组织由铁素体和球状渗碳体组成。A_1以下接头的小夏比冲击试验吸收能量提高了3倍。

项目成果

超硬合金ツールを用いた高けい素球場黒鉛鋳鉄とフェライト系ステンレス鋼との摩擦攪拌接合

使用硬质合金工具搅拌高硅石墨铸铁和铁素体不锈钢的摩擦焊

• 发表时间: 2010
• 作者: 河内美穂子;金内一徳;長谷川徹雄;鄭永東;藤井英俊;晴山巧
• 通讯作者: 晴山巧

A Two-step Rotation Bonding of 6061Al and 5052 Al Alloys

6061Al和5052铝合金的两步旋转连接

• 发表时间: 2010
• 作者: Y.F.Sun;H.Fujii;N.Takaki;Y.Okitsu
• 通讯作者: Y.Okitsu

レーザクラッディング層への摩擦攪拌プロセスによるナノ工具鋼被膜の創製

激光熔覆层上搅拌摩擦工艺制备纳米工具钢涂层

• 发表时间: 2010
• 作者: 森貞好昭;長岡亨;福角真男;藤井英俊;北村優介;水野雅;阿部源隆
• 通讯作者: 阿部源隆

摩擦攪拌を利用したオーステナイト系ステンレス鋼の表面改質

利用搅拌摩擦对奥氏体不锈钢进行表面改性

• 发表时间: 2010
• 作者: 土屋由美子;高橋雅士;斎藤宣久;藤井英俊
• 通讯作者: 藤井英俊

高周波誘導加熱方式を用いた炭素鋼の摩擦攪拌接合

高频感应加热碳钢搅拌摩擦焊

• 发表时间: 2010
• 作者: 洪尚填;藤井英俊;田崎潤;杉田薫
• 通讯作者: 杉田薫