Separation and recovery of rare metals by using iron-and steelmaking processes

利用炼铁和炼钢工艺分离和回收稀有金属

• 批准号: 20360343
• 负责人: INOUE RYO
• 金额: $ 12.48万
• 依托单位: Tohoku University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (B)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2010
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20360343/
• 关键词: レアメタル; 鉄鋼製造プロセス; 還元; 酸化; 分離; ニオブ; バナジウム; 溶銑予備処理スラグ; 転炉スラグ; 鉱物相; 濃化; 溶解度; 炭化物生成; 高炉スラグ; 炭素還元; ニオブ分配比

It has been found from the V solubility in pig iron and the distribution ratio between BF slag and pig iron that V in iron ore moves to molten pig iron without carbide precipitation. V and Nb were easily contained in FeO-containing slag in the hot metal pretreatment and BOF process. V concentrated in calcium silicate and CaO-FeO-Al_2O_3 phases, Nb concentrated in CaO-FeO-Al_2O_3 phase, and P concentrated in calcium silicate phase during cooling of slag. Therefore, it was expected that the ore substitute including large amounts of V, Nb and P could be obtained by separating those mineral phases from the other slag phases.

从V在生铁中的溶解度和高炉渣与生铁之间的分配比可以看出，铁矿石中的V在没有碳化物析出的情况下向生铁熔体迁移。在铁水前处理和转炉冶炼过程中，含FeO渣中容易含有V和Nb。在炉渣冷却过程中，V集中在硅酸钙和CaO-FeO-Al_2O_3相中，Nb集中在CaO-FeO-Al_2O_3相中，P集中在硅酸钙相中。因此，通过将这些矿物相与其他渣相分离，可以得到含有大量V、Nb、P的代矿产品。

项目成果

貴金属・レアメタルの現状と課題

贵金属和稀有金属的现状和问题

• 发表时间: 2010
• 期刊: 化学工学
• 作者: Yoshihiro Kamimura;Kengo Miyoshi;Ken-ichi Kurumada;岡部徹
• 通讯作者: 岡部徹

金属(化合物)粉の選び方・使い方 第1章(一般的な金属粉・金属化合物/レアメタル粉体の特性・物性)

如何选择和使用金属（化合物）粉末第一章（常见金属粉末、金属化合物、稀有金属粉末的特性和物理性能）

• 发表时间: 2010
• 作者: 野瀬勝弘;岡部徹
• 通讯作者: 岡部徹

レアメタルを巡る誤解を解く

消除对稀有金属的误解

• 发表时间: 2010
• 期刊: OHM
• 作者: 岡部徹;中村崇
• 通讯作者: 中村崇

レアメタル製造のプロセス技術

稀有金属生产工艺技术

• 发表时间: 2010
• 期刊: OHM
• 作者: 岡部徹;野瀬勝弘
• 通讯作者: 野瀬勝弘

レアメタルの現状と展望

稀有金属现状及前景

• 发表时间: 2010
• 期刊: 電気協会報
• 作者: 野瀬勝弘;岡部徹
• 通讯作者: 岡部徹