Development of super hard Ti-B-C coated tool with high thermal stability for dry cutting.

开发用于干切削的高热稳定性超硬Ti-B-C涂层刀具。

• 批准号: 20560114
• 负责人: KOHZAKI Masao
• 金额: $ 3.16万
• 依托单位: Tokai University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2010
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20560114/
• 关键词: 切削加工; コーテッド工具; Ti合金; 薄膜; スパッタリング; チタン; ホウ素; 炭素

In this work, the hardness and the frictional properties of Ti-B-C films have been improved by controlling the contents of boron and carbon. TiB_<2+α> films obtained with TiB_2+10wt%B target had the high hardness above 35GPa. The friction coefficients of Ti-B-C films with the carbon content above 40% were about 0.2. In the cutting Ti alloys, tip formation process had been improved and the surface roughness of the work piece became smooth by using the Ti-B-C coated tools.

本工作通过控制硼和碳的含量来提高Ti-B-C薄膜的硬度和摩擦性能。用TiB_2+10wt%B靶制备的TiB_（2+α）薄膜具有35 GPa以上的高硬度。碳含量大于40%的Ti-B-C薄膜的摩擦系数约为0.2。在切削钛合金时，Ti-B-C涂层刀具改善了刀尖成形工艺，使工件表面粗糙度变得光滑。

项目成果

高耐熱B-C-X系硬質膜を用いた難削材の高効率精密加工

使用高耐热B-C-X硬质薄膜对难切削材料进行高效精密加工

• 发表时间: 2009
• 期刊: 東海大学紀要工学部 49
• 作者: 金井政樹;平田敦;神崎昌郎;神崎昌郎
• 通讯作者: 神崎昌郎

ホームページ等。

主页等

高耐熱B-C-X系硬質膜を用いた難削材の高効率加工

使用高耐热B-C-X硬质薄膜，高效加工难切削材料

• 发表时间: 2009
• 期刊: 東海大学紀要工学部 Vol.49, No.2
• 作者: 金井政樹;平田敦;神崎昌郎
• 通讯作者: 神崎昌郎

Development of High Adhesive and Lubricious Ti-B-C Thin Films for Cutting of Ti Alloys

钛合金切削用高附着力润滑Ti-B-C薄膜的研制

• 发表时间: 2009
• 作者: 金井政樹;平田敦;Shouichi Inaba
• 通讯作者: Shouichi Inaba

航空機用材料の加工に適したホウ素含有潤滑性硬質膜の創成およびそのドライ加工性能

适合航空材料加工的含硼润滑硬膜的制备及其干加工性能

• 发表时间: 2010
• 作者: Satoru Maegawa;Atsushi Suzuki;Ken Nakano;稲葉翔一,神崎昌郎
• 通讯作者: 稲葉翔一,神崎昌郎