Creation of new environmental clean-up material by effect of size of layered double hydroxide

利用层状双氢氧化物尺寸效应创建新型环境净化材料

• 批准号: 20560755
• 负责人: YAMAZAKI Atsushi
• 金额: $ 3万
• 依托单位: Waseda University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2010
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20560755/
• 关键词: ハイドロタルサイト; 層状複水酸化物; シモンコライト; 陰イオン交換; イオン; 吸着固定; ナノサイズ; 排水処理; 素材資源; 地層汚染修復; イオン吸着固定

Layered double hydroxide (LDH) adjusted the crystallite size to less than 20nm was synthesized in Mg-Al and Fe-Zn systems. The LDHs were able to adsorb and to fix the contained harmful negative ions in drainage effectively. The simonkolleite type material that had the bridge structure was selectively formed in a point near the Zn end member of the Fe-Zn system, and selectivity was admitted for Cr (VI) ion. Moreover, it was shown to reproduce in former LDH that had adsorption and the exchangeability of about 95% by the restructuring method.

在Mg-Al和Fe-Zn体系中合成了层状双氢氧化物(LDH)，将晶粒尺寸调整至小于20nm。 LDHs能够有效吸附并固定排水中的有害负离子。在Fe-Zn系的Zn端元附近的点选择性地形成具有桥结构的硅锰矿型材料，并且对于Cr(VI)离子也具有选择性。另外，通过重组法，可以在吸附性和交换性达到95%左右的原LDH中再现。

项目成果

Zn-Fe系simonkolleite型物質の結晶化学的特性

Zn-Fe基硅锰矿型材料的晶体化学性质

• 发表时间: 2010
• 作者: 大野睦浩;杉山周平;横田季彦;山崎淳司;家村武志
• 通讯作者: 家村武志

NLDH/微結晶質層状複水酸化物を使った水処理システム

使用NLDH/微晶层状双氢氧化物的水处理系统

• 发表时间: 2011
• 期刊: 粘土科学 Vol.49、No.3
• 作者: 大野睦浩;杉山周平;横田季彦;山崎淳司
• 通讯作者: 山崎淳司

NLDH/微結晶性層状複水酸化物を使った水処理システム

使用NLDH/微晶层状双氢氧化物的水处理系统

• 发表时间: 2010
• 作者: T.Hongo、Y.Inoue;A.Yamazaki;大野睦浩
• 通讯作者: 大野睦浩

Zn-Fe系simonkollite型物質の結晶化学的特性

Zn-Fe基硅锰矿型材料的晶体化学性质

• 发表时间: 2008
• 作者: 家村武志;本郷輝久;山崎淳司
• 通讯作者: 山崎淳司

Mechanochemical treatment of hydrotalcite in vibration milling and its effect on fluoride adsorption ability

振动磨水滑石的机械化学处理及其对氟吸附能力的影响

• 发表时间: 2010
• 期刊: Clay Science Vol.14、No.5
• 作者: T.Hongo、Y.Inoue;A.Yamazaki
• 通讯作者: A.Yamazaki