Study on formation processes of noble metal composite nanoparticles by radiation-induced reduction

辐射还原贵金属复合纳米粒子形成过程研究

• 批准号: 20760596
• 负责人: KOJIMA Takao
• 金额: $ 2.75万
• 依托单位: Osaka Prefecture University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2009
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20760596/
• 关键词: 放射線還元場; 貴金属複合ナノ粒子; パルスラジオリシス; 短寿命活性種

Radiation-induced synthesis of composite nanoparticles consisting of noble metals and ceramics in an aqueous solution system has been investigated. In this work, radiation-induced formation processes of noble metal composite nanoparticles in aqueous solutions were observed by UV-vis absorption spectroscopy. The influence of temperature and other factors on growth curves of surface plasmon peak of noble metal nanoparticles was observed. The relation between kinetics of formation process and condition in aqueous solution was discussed.

研究了在水溶液体系中由贵金属和陶瓷组成的复合纳米颗粒的辐射诱导合成。在这项工作中，通过紫外-可见吸收光谱观察了贵金属复合纳米颗粒在水溶液中的辐射诱导形成过程。观察温度等因素对贵金属纳米粒子表面等离子体峰生长曲线的影响。讨论了水溶液中形成过程的动力学与条件之间的关系。

项目成果

放射線誘起還元により生成した金ナノ粒子の凝集過程

辐射诱导还原生成金纳米颗粒的聚集过程

• 发表时间: 2010
• 作者: 小嶋崇夫;清野智史;谷口良一;奥田修一;山本孝夫
• 通讯作者: 山本孝夫

Synthesis of Au-Pd bimetallic nanoparticles under energetic irradiation fields

• DOI: 10.1016/j.radphyschem.2009.05.007
• 发表时间: 2009-12-01
• 期刊: RADIATION PHYSICS AND CHEMISTRY
• 影响因子: 2.9
• 作者: Taguchi, N.;Iwase, A.;Hori, F.
• 通讯作者: Hori, F.

Radiation-induced synthetic process of Au composite nanoparticles in aqueous solution

水溶液中辐射诱导合成金复合纳米粒子的过程

• 发表时间: 2008
• 作者: T. Kojima;S. Seino;T.A. Yamamoto;T. Shibano;A. Iwase;R. Taniguchi;S. Okuda
• 通讯作者: S. Okuda

放射線誘起還元場における貴金属複合ナノ粒子生成過程の温度依存性

辐射诱导还原场中贵金属复合纳米颗粒形成过程的温度依赖性

• 发表时间: 2009
• 作者: 小嶋崇夫;清野智史;谷口良一;奥田修一;山本孝夫
• 通讯作者: 山本孝夫