The use of xenon for synthesis of new carbon materials and analysis of microporous structure

氙用于新型碳材料的合成及微孔结构分析

• 批准号: 20750166
• 负责人: GOTOH Kazuma
• 金额: $ 2.83万
• 依托单位: Okayama University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2009
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20750166/
• 关键词: 炭素; キセノン; アモルファス; 細孔解析; 酸化黒鉛; 炭素材料; 核磁気共鳴; ハードカーボン; 金属ナノ粒子

This research showed that pore structure of amorphous carbon can be evaluated using xenon and Xe NMR. Xenon also can be used for improvement of carbon surface. On the other hand, porous graphene materials having platinum, ruthenium or palladium nanoparticles on exfoliated graphene sheets were produced from graphite oxide and metal complexes. The research showed that the samples have catalytic activity for some reactions, for example, oxygen reduction reaction on full cell.

本研究表明，无定形碳的孔结构可以使用氙和1H NMR进行评估。氙也可用于改善碳表面。另一方面，由氧化石墨和金属络合物制备在剥离的石墨烯片上具有铂、钌或钯纳米颗粒的多孔石墨烯材料。研究表明，样品对某些反应具有催化活性，如全电池上的氧还原反应。

项目成果

Observation of micropores in hard-carbon using 129Xe NMR porosimetry

使用 129Xe NMR 孔隙度测定法观察硬碳中的微孔

• 发表时间: 2008
• 期刊: J. Phys. Chem. Sol. 69
• 作者: K. Gotoh;T. Ueda;H. Omi;T. Eguchi;M. Maeda;M. Miyahara;A. Nagai;H. Ishida
• 通讯作者: H. Ishida

金および銀ナノ粒子を担持するグラフェンの作製

负载金银纳米粒子的石墨烯的制备

• 发表时间: 2010
• 作者: 後藤和馬;山本亜季;衣本太郎;藤井英司;大久保貴広;石田祐之
• 通讯作者: 石田祐之

クロラニル酸-1, 3-ジアジン(1/1)塩-水和物および(1/2)塩の結晶構造と相転移

氯苯甲酸-1,3-二嗪(1/1)盐水合物和(1/2)盐的晶体结构和相变

• 发表时间: 2010
• 作者: 後藤和馬;浅地哲夫;石田祐之
• 通讯作者: 石田祐之

酸化グラファイトを用いた白金ナノ粒子を含む多孔質炭素材料の開発

使用氧化石墨开发含有铂纳米颗粒的多孔碳材料

• 发表时间: 2008
• 作者: 後藤和馬;森重國光;川端浩二;藤井英司;河田卓也;石田祐之
• 通讯作者: 石田祐之

多孔質炭素材料およびその製造方法ならびに燃料電池

多孔碳材料及其制造方法和燃料电池

• 发表时间: 2008