Optimum formation of nanotribofilm by the self-lubricated ion implanted layer

自润滑离子注入层纳米摩擦膜的最佳形成

• 批准号: 20760102
• 负责人: AOKI Saiko
• 金额: $ 2.75万
• 依托单位: Tokyo Metropolitan Industrial Technology Research Institute
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2009
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20760102/
• 关键词: トライボロジー; 潤滑油の物理化学; 境界摩擦; 表面改質; トライボフィルム; イオン注入; 摩擦摩耗特性; 潤滑油; リン; 硫黄; 窒素

The aim of the study is to improve the friction reduction effect and the antiwear performance of tribofilms, formed by lubricating additives, with ion implantations. Phosphorous and sulphur ions were respectively implanted into steel specimens, and then the friction measurement, surface analyses and observations were performed to elucidate the effect of ion implantations on the friction characteristics of steel lubricated by oil. Higher value of the ion doses provided higher concentration of the ions into the specimens, resulting in lower both friction coefficient and wear rate of the specimens. This study demonstrated ion implantations can reduce friction and wear.

研究了离子表面修饰对润滑添加剂摩擦膜减摩效果和抗磨性能的影响。将磷离子和硫离子分别注入钢试样中，然后进行摩擦测量、表面分析和观察，以阐明离子注入对油润滑钢摩擦特性的影响。离子注入量越大，注入试样的离子浓度越高，试样的摩擦系数和磨损率越低。研究表明，离子表面处理可以减少摩擦和磨损。

项目成果

Comparison of Sliding Friction and Wear Characteristics among ASTM D2 Tool Steels Implanted Different Elements by Plasma Ion Immersion Implantation

等离子离子浸渗注入不同元素的 ASTM D2 工具钢滑动摩擦和磨损特性比较

• 发表时间: 2009
• 期刊: NETSU SHORI (Journal of The Japan Society for Heat Treatment) 49
• 作者: Saiko Aoki;Masahiro Kawaguchi;Yoshikazu Teranishi;Atsushi Mitsuo;Masabumi Masuko
• 通讯作者: Masabumi Masuko

プラズマイオン注入法により鋼表面に注入された元素イオンの潤滑性能評価

等离子体离子注入法注入钢表面元素离子润滑性能评价

• 发表时间: 2008
• 期刊: トライボロジー会議予稿集(名古屋) 2008-9
• 作者: 平山朋子;佐々木勝美;矢部寛;青木才子,川口雅弘,三尾淳,鈴木章仁,益子正文
• 通讯作者: 青木才子,川口雅弘,三尾淳,鈴木章仁,益子正文

Tribological Properties of Steel Modified by Sulfur Ion Implantation

硫离子注入改性钢的摩擦学性能

• 发表时间: 2009
• 作者: aiko Aoki;Yoshikazu Teranishi;Masahiro Kawaguchi;Atsushi Mitsuo
• 通讯作者: Atsushi Mitsuo

Friction Characteristics of Phosphorous-containing Steel Surface Derived from Ion Implantation

离子注入含磷钢表面摩擦特性

• 发表时间: 2010
• 期刊: Journal of Tribology, Proceedings of the Institution of Mechanical Engineers, Part J
• 作者: Saiko Aoki;Yoshikazu Teranishi;Atsushi Mitsuo;Masahiro Kawaguchi;Kazuo;Morikawa;Akihito Suzuki;Masabumi Masuko
• 通讯作者: Masabumi Masuko

鋼の境界摩擦特性に及ぼすリンイオン注入の影響

磷离子注入对钢边界摩擦性能的影响

• 发表时间: 2009
• 作者: 青木才子;寺西義一;川口雅弘;三尾淳;鈴木章仁;益子正文
• 通讯作者: 益子正文