Fabrication of visible-light active TiO_2 nanotubular layers by electrochemical processes and their characterization

电化学过程制备可见光活性TiO_2纳米管层及其表征

• 批准号: 20760493
• 负责人: TSUCHIYA Hiroaki
• 金额: $ 2.66万
• 依托单位: Osaka University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2009
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20760493/
• 关键词: 酸化チタン; ナノチューブ; アノード酸化; 可視光応答化; 結晶化

The present work explores new processes for the crystallization of anodic TiO_2 nanotube layers and the nitrogen-doping into TiO_2 nanotube layers. TiO_2 nanotube layers prepared are also characterized. After the two-step anodization nocrystallization takes place within nanotube layers whereas anodization in organic electrolytes at elevated temperatures leads to the partial crystallization of anodic TiO_2 nanotubes. Nitrogen-doped TiO_2 nanotube layers formed by anodization of nitrogen containing Ti alloys exhibit visible light photocatalytic activities.

本工作探索了阳极TiO_2纳米管层的晶化和氮掺杂的新工艺。对制备的TiO_2纳米管层进行了表征。两步阳极氧化后，纳米管层内没有发生结晶，而在有机电解液中高温阳极氧化导致阳极TiO_2纳米管的部分结晶。含氮钛合金阳极氧化制备的氮掺杂TiO_2纳米管具有可见光催化活性。

项目成果

Anodic Porous and Tubular Oxide Layers on Ti Alloys

钛合金上的阳极多孔和管状氧化层

• 发表时间: 2008
• 作者: ハフィザル ビンヤハヤ;栗山恵司;崎田博文;生駒嘉史;本岡輝昭;H. Tsuchiya
• 通讯作者: H. Tsuchiya

アノード酸化により形成する酸化物層の形態・構造に及ぼす基板組成の影響

基体成分对阳极氧化氧化层形貌和结构的影响

• 发表时间: 2008
• 作者: Kentaro Shinoda;Hideyuki Murakami;Seiji Kuroda;Kohsei Takehara;Hiroaki Tsuchiya;土谷博昭
• 通讯作者: 土谷博昭

電気化学プロセスを用いた自己組織化ポーラス酸化物の創製

使用电化学过程创建自组装多孔氧化物

• 发表时间: 2008
• 作者: H.Tsuchiya;T.Akaki;Y.Koizumi;Y.Minamino;S.Fujimoto;Yousuke Kawahito;土谷博昭
• 通讯作者: 土谷博昭

アノード酸化によりバルブ金属合金上に形成する酸化物ナノポーラス・ナノチユーブ層

阳极氧化在阀金属合金上形成氧化物纳米孔纳米管层

• 发表时间: 2008
• 作者: ハフィザルビンヤハヤ;栗山恵司;崎田博文;生駒嘉史;本岡輝昭;土谷博昭
• 通讯作者: 土谷博昭

有機溶媒のでの陽極酸化TiO_2ナノチューブ層形成プロセスの検討

有机溶剂中阳极氧化TiO_2纳米管层形成过程的研究

• 发表时间: 2010
• 作者: 清水康智;土谷博昭;藤本慎司
• 通讯作者: 藤本慎司