Self-damage detection composite structure using thermal deformation caused by Joule heating

利用焦耳热引起的热变形检测自损伤复合结构

• 批准号: 21560079
• 负责人: TODOROKI Akira
• 金额: $ 3万
• 依托单位: Tokyo Institute of Technology
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21560079/
• 关键词: 破壊; 複合材料; CFRP; 層間はく離; 電気抵抗; ジュール発熱; モニタリング; 落錘試験; 損傷検知; ジュール加熱; 損傷; 有限要素法

Self-sensing method is focused on here. In the present study, statistical monitoring method is applied for the electrical resistance changes of several segments before and after the Joule heating. After Joule heating, electrical resistances of several segments are measured. Using the statistical similarity tests, the damaged area of the CFRP is detected. The method is applied to the CFRP plates here. Impact load tests were performed and damage at the electrode was also performed here. The method is experimentally proved to be effective for the detection of the delamination cracks.

本文重点介绍了自感知方法。在本研究中，统计监测方法应用于焦耳加热前后的几个部分的电阻变化。焦耳加热后，测量几个段的电阻。利用统计相似性检验，检测出CFRP的损伤区域。本文将该方法应用于CFRP板。进行了冲击负荷试验，并在此进行了电极损坏试验。实验证明，该方法对分层裂纹的检测是有效的。

项目成果

抵抗温度特性変化を利用したCFRP平板の統計的層間はく離検出

利用电阻温度特性变化统计CFRP平板分层检测

• 发表时间: 2010
• 期刊: 日本機械学会論文集, A編
• 作者: 鈴木良郎;轟章;高橋航圭;水谷義弘;松崎亮介
• 通讯作者: 松崎亮介

Impact Damage Detection in CFRP Using Statistical Analysis of Resistance-Temperature Characteristics

• DOI: 10.1299/jmmp.5.33
• 发表时间: 2011
• 期刊: Journal of Solid Mechanics and Materials Engineering
• 作者: Yoshiro Suzuki;A. Todoroki;Y. Mizutani;R. Matsuzaki

健全データ学習不要の電気抵抗変化法によるCFRP平板の統計的損傷

在没有良好数据学习的情况下，使用电阻变化法统计CFRP平板的损伤

• 发表时间: 2011
• 期刊: 日本機械学会論文集A編
• 作者: 鈴木良郎;轟章;水谷義弘;松崎亮介
• 通讯作者: 松崎亮介

抵抗温度特性変化利用の電気抵抗変化法によるCFRPの無学習損傷診断

利用电阻温度特性变化的电阻变化法进行CFRP损伤诊断的学习

• 发表时间: 2010
• 作者: 保國惠一;速水謙;鈴木良郎
• 通讯作者: 鈴木良郎