Allowable crack depth of concrete members suffered earthquake load

受地震荷载作用的混凝土构件允许裂缝深度

• 批准号: 21560590
• 负责人: KISHIMOTO Ichizo
• 金额: $ 2.83万
• 依托单位: Kinki University (2011)Osaka University (2009-2010)
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21560590/
• 关键词: 鉄筋コンクリート; 残留ひび割れ幅; 鉄筋腐食; 塩化物イオン濃度; 柱、梁部材; ひび割れ間隔; 鉄筋付着; 解析プログラム; ひび割れ幅

The method to estimate residual crack width on concrete members suffered earthquake load was studied by experimental and analytical investigations and the calculation formula to calculate residual crack width was derived. By experimental study the relation between crack width on the surface of concrete member and degree of corrosion on steel bars, Cl-ion concentration are studied. 0.2mm more over crack width caused increasing Cl-ion concentration in the cracking surface of concrete and degree of corrosion of steel bars equipped in concrete.

通过试验研究和分析研究，研究了地震作用下混凝土构件残余裂缝宽度的估算方法，推导了计算残余裂缝宽度的计算公式。通过试验研究，研究了混凝土构件表面裂缝宽度与钢筋锈蚀程度、氯离子浓度的关系。裂缝宽度超过0.2 mm时，混凝土裂缝表面的氯离子浓度增加，混凝土内钢筋的锈蚀程度增大。

项目成果

曲げとせん断を受けるRC部材の曲げひび割れ発生位置に関する考察

受弯剪作用的钢筋混凝土构件弯曲裂缝位置的考虑

• 发表时间: 2010
• 期刊: コンクリート工学年次論文報告集
• 作者: 増田有佑;南口真一;岸本一蔵
• 通讯作者: 岸本一蔵

試験方法の違いによるひび割れ内部の鉄筋腐食に関する研究

不同试验方法对裂纹内钢筋腐蚀的研究

• 发表时间: 2012
• 期刊: 日本建築学会近畿支部研究報告集
• 作者: 三品雄資;秋元秀孝;岸本一蔵
• 通讯作者: 岸本一蔵

曲ひび割れを有する鉄筋コンクリート部材の腐食に関する研究

弯曲裂缝钢筋混凝土构件腐蚀研究

• 发表时间: 2011
• 作者: 修行稔;島津勝;山田良子;徳光美紗代;野口博;南口真一;秋元秀孝
• 通讯作者: 秋元秀孝

ひび割れを有する鉄筋コンクリート部材の腐食に関する実験的研究

含裂缝钢筋混凝土构件腐蚀试验研究

• 发表时间: 2012
• 期刊: コンクリート工学年次論文報告集
• 作者: 秋元秀孝;岸本一蔵
• 通讯作者: 岸本一蔵

ひび割れを有する鉄筋コンクリート部材の鉄筋腐食に関する実験的研究

含裂缝钢筋混凝土构件中钢筋锈蚀试验研究

• 发表时间: 2011
• 作者: H.G.Kim;S.Yoshitomi;M.Tsuji;I.Takewaki;秋元秀孝
• 通讯作者: 秋元秀孝