Development of self-healing anti-corrosion coatings using functional nanomaterials

利用功能纳米材料开发自修复防腐涂料

• 批准号: 21560747
• 负责人: YABUKI Akihiro
• 金额: $ 3.24万
• 依托单位: Hiroshima University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21560747/
• 关键词: ナノ材料; 自己修復性; コーティング; 皮膜; 金属材料; 腐食; 防食; アルミニウム; マグネシウム

Self-healing coatings using functional nanomaterials and organic healing agents were developed to prevent corrosion of metallic materials. Nanomaterials(nanoparticles, nanofibers, nanoflakes) and organic healing agents were added in polymer, and these were coated on the surface of metallic materials. Corrosion tests of scratched coatings were conducted. Corrosion resistance of the specimen increased, resulting in self-healing capability of the coatings. Coatings of nanoporous materials and healing agents also showed self-healing capability. The healing film of organic healing agents could be observed on the scratched surface of specimen after corrosion test.

为了防止金属材料的腐蚀，开发了使用功能性纳米材料和有机修复剂的自修复涂层。将纳米材料（纳米颗粒、纳米纤维、纳米片）和有机修复剂加入聚合物中，并将其涂覆在金属材料表面。进行了划痕涂层的腐蚀试验。试样的耐腐蚀性提高，导致涂层的自修复能力。纳米多孔材料和修复剂的涂层也表现出自修复能力。腐蚀试验后，在划痕表面可观察到有机修复剂的修复膜。

项目成果

自己修復（キズ復元）材料の最新技術、メーカー採用のトレンド

自愈（划痕修复）材料的最新技术以及制造商采用的趋势

• 发表时间: 2011
• 作者: Wada;Takehiko;藤村 幸次郎，大内 誠，澤本 光男;原田明・高島義徳
• 通讯作者: 原田明・高島義徳

Barrier and self-healing coating with fluoro-organic compound for zinc

含氟有机锌化合物阻隔和自修复涂层

• 期刊: Materials and Corrosion (in press)
• 作者: Akihiro Yabuki;Ryo Kaneda
• 通讯作者: Ryo Kaneda

Self-Healing Corrosion Protective Coatings by Oxide Particles and a pH-Sensitive Organic Agent on a Magnesium Alloy

镁合金上氧化物颗粒和 pH 敏感有机剂的自修复腐蚀防护涂层

• 发表时间: 2010
• 作者: Akihiro Yabuki;Mariko Sakai
• 通讯作者: Mariko Sakai

高分子多孔膜を用いた自己修復性耐食コーティング

使用多孔聚合物膜的自修复耐腐蚀涂层

• 发表时间: 2010
• 作者: 西坂俊則;矢吹彰広
• 通讯作者: 矢吹彰広

微粒子コンポジットポリマーによる自己修復性耐食コーティング

颗粒复合聚合物自修复耐腐蚀涂层

• 发表时间: 2009
• 作者: 西坂俊則;矢吹彰広
• 通讯作者: 矢吹彰広