Creation of phase-separated silicate glasses containing Cu cluster ions for luminous materials applied to white color LED.

创建含有 Cu 簇离子的相分离硅酸盐玻璃，用于白色 LED 的发光材料。

• 批准号: 21360326
• 负责人: YASUMORI Atsuo
• 金额: $ 11.4万
• 依托单位: Tokyo University of Science
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (B)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21360326/
• 关键词: 機能性ガラス; 発光; ホウケイ酸塩ガラス; 銅イオン; 分相; クラスタ; 発光ダイオード; 白色発光; アルカリホウケイ酸系ガラス; 近紫外光; 溶融急冷法; 蛍光スペクトル; 励起スペクトル

The phase-separated alkali metal-borosilicate glasses containing Cu^+clusters which exhibit warm color yellow luminescence under irradiation of ultraviolet(UV) LED light were prepared by use of a conventional melting method in order to achieve high power luminous material having high thermal and UV light stability. The obtained glass showed yellow luminescence of around 600 nm. The emission intensity increased largely by optimizing additive amounts of Cu ions and a reducing agent. The emission intensity increased much higher by incorporation of calcium oxide into the glass composition.

通过使用传统的熔融方法，制备了含有Cu^+簇的相分离的碱金属硅酸盐玻璃，这些玻璃杯在紫外线（UV）LED灯光下表现出温暖的黄色发光，通过使用传统的熔融方法来制备，以实现具有高热量和UV光稳定性的高功率发光材料。获得的玻璃显示出约600 nm的黄色发光。发射强度在很大程度上通过优化添加量的Cu离子和还原剂来增加。通过将氧化钙掺入玻璃成分中，发射强度提高了得多。

项目成果

Photo luminescence properties of copper ion doped alkali borosilicate glasses in metastable immiscibility region.

铜离子掺杂碱金属硼硅酸盐玻璃在亚稳态不混溶区的光致发光特性。

• 发表时间: 2010
• 作者: 山田裕樹;八島正知;石原辰已;Sirikanda Nuansaeng;Atsuo Yasumori
• 通讯作者: Atsuo Yasumori

発光ガラス及び当該発光ガラスを備えた発光装置

发光玻璃及具备该发光玻璃的发光装置

• 发表时间: 2009

特許

专利

• 发表时间: 2008