Effect of Viscosity on Fatigue Strength of Concrete in Liquid

粘度对液体中混凝土疲劳强度的影响

• 批准号: 21760362
• 负责人: TSUNOKAKE Hisao
• 金额: $ 2.83万
• 依托单位: Osaka City University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2010
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21760362/
• 关键词: コンクリート構造; 疲労強度; 疲労試験; 疲労寿命; 液体圧力; ひび割れ; コンクリート

This study describes flexural shear cyclic loading test results of reinforced concrete member in various viscous liquid, with focusing on fatigue characteristic due to liquid permeation into cracks of the member. As a result, it was obtained that the viscous difference of liquid influences crack progress and fatigue strength. Furthermore, it was obtained that the fatigue life is affected by the difference of rate of cyclic loading.

本文介绍了钢筋混凝土构件在不同粘性液体中的弯曲剪切循环加载试验结果，重点研究了液体渗入构件裂缝时的疲劳特性。结果表明，液体粘性差对裂纹扩展和疲劳强度有影响。此外，还得到了循环加载速率的不同对疲劳寿命的影响。

项目成果

ひび割れを有するRC 部材の液中引張疲労実験

含裂纹钢筋混凝土构件水下拉伸疲劳试验

• 发表时间: 2010
• 期刊: 土木学会第65回年次学術講演会講演概要集 Vol.65
• 作者: 上田真彦;角掛久雄;大内一
• 通讯作者: 大内一

浸漬した無補強RC梁の疲労寿命に及ぼす載荷速度の影響

加载速率对沉入式无筋RC梁疲劳寿命的影响

• 发表时间: 2010
• 期刊: 土木学会第65回年次学術講演会講演概要集 Vol.65
• 作者: 角掛久雄;大内一
• 通讯作者: 大内一