Development of the Dental Ceramic Material with Ca modified TiO_2 Nano-tubes

Ca修饰TiO_2纳米管牙科陶瓷材料的研制

• 批准号: 21791956
• 负责人: NISHIDA Hisataka
• 金额: $ 2.66万
• 依托单位: Osaka Dental University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2010
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21791956/
• 关键词: セラミックス; 酸化チタン; ナノチューブ; 生体材料; 骨代替材料; 水熱合成

It is reported that the bone fracture often happened at the part in which the bone replacement material was filled. This is because not only the poor mechanical strength of bone replacement materials but also the bone regeneration ability of them is inferior compared with autogenous bone. We found that TiO_2 nanotube bonded to the cell and activated osteoblast without addition of biochemical factor in previous studies. The aim of this study was to develop the materials that promote the cell bonding , proliferation and differentiation by making Ca modified TiO_2 nanotube by hydrothermal synthesis.

据报道，骨折往往发生在骨替代材料的填充处。这是因为与自体骨相比，骨替代材料不仅机械强度差，而且骨再生能力也较差。我们在以往的研究中发现，在没有添加生化因子的情况下，二氧化钛纳米管可以与细胞结合并激活成骨细胞。本研究的目的是通过水热合成法制备钙修饰的二氧化钛纳米管，以开发促进细胞结合、增殖和分化的材料。

项目成果

Making TiO2 Nanotubes Inducing Osteoblast Activation by hydrothermal synthesis.

通过水热合成制备诱导成骨细胞活化的 TiO2 纳米管。

• 发表时间: 2010
• 作者: Nishida H;Sekino T;Nakamura T;Yamamoto K.
• 通讯作者: Yamamoto K.

Making TiO2 Nano-Tubes Inducing Osteoblast Activation by Hydrothermal Synthesis

通过水热合成制备诱导成骨细胞活化的 TiO2 纳米管

• 发表时间: 2010
• 作者: Nishida H;Sekino T;Nakamura T;Yamamoto K.;西田尚敬
• 通讯作者: 西田尚敬

チタン金属表面における酸化チタンナノチューブの合成と生体適合性.

钛金属表面氧化钛纳米管的合成及其生物相容性。

• 发表时间: 2009
• 作者: 西田尚敬;江草宏;中村隆志;矢谷博文;山本一世.
• 通讯作者: 山本一世.

低温化学合成法によるチタニアナノチューブの析出と生体適合性.

低温化学合成二氧化钛纳米管的沉淀和生物相容性。

• 发表时间: 2009
• 作者: 西田尚敬;江草宏;三浦治郎;中村隆志;矢谷博文;山本一世.
• 通讯作者: 山本一世.

低温化学合成法によるチタニアナノチューブの析出と生体適合性

低温化学合成法沉淀二氧化钛纳米管及其生物相容性

• 发表时间: 2009
• 作者: 西田尚敬;江草宏;三浦治郎;中村隆志;矢谷博文;山本一世.;西田尚敬
• 通讯作者: 西田尚敬