Dynamics on volatilization of metal compounds accompanied by heterogeneous chemical reactions in molten slag of wastes

废弃物熔渣中非均相化学反应金属化合物挥发动态

• 批准号: 22560758
• 负责人: MATSUDA Hitoki
• 金额: $ 2.83万
• 依托单位: Nagoya University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22560758/
• 关键词: 反応速度; 廃棄物; 溶融スラグ; 重金属; 揮発分離; 溶融処理; 硫化水素; 酸化鉛; 塩化水素

Dynamics studies on volatilization of lead compounds from SiO_2-Al_2O_3-CaO molten slag, accompanied by chlorination and sulfidation reactions of PbO with Cl and S compounds, were conducted. Results showed that the volatilization of lead compounds of lower boiling temperatures which were produced by the reaction of PbO with coexisting inorganic chlorides or HCl and H_2S gas was promoted. Results also showed that the rates of volatilization of lead compounds were higher from molten slag of lower viscosity with higher CaO content.

研究了SiO_2-Al_2O_3-CaO系熔渣中铅化合物挥发及PbO与Cl、S化合物氯化、硫化反应的动力学。结果表明，PbO与无机氯化物或HCl和H_2S气体反应生成的低沸点铅化合物的挥发被促进。结果还表明，高CaO含量的熔渣粘度越低，铅化合物的挥发速率越大。

项目成果

N_2-H_2S 雰囲気におけるCaO-SiO_2-Al_2O_3溶融スラグからの鉛の揮発挙動

N_2-H_2S气氛中CaO-SiO_2-Al_2O_3熔渣中铅的挥发行为

• 发表时间: 2013
• 期刊: 廃棄物資源循環学会誌
• 作者: Kageyama Hiroki;Osada Shohichi;Nakata Hiroyuki;Kubota Mitsuhiro;Matsuda Hitoki;景山広樹,長田昭一,窪田光宏,松田仁樹
• 通讯作者: 景山広樹,長田昭一,窪田光宏,松田仁樹

N2-H2S 雰囲気におけるCaO-SiO2-Al2O3溶融スラグからの鉛の揮発挙動

N2-H2S气氛中CaO-SiO2-Al2O3熔渣中铅的挥发行为

• 发表时间: 2013
• 期刊: 廃棄物資源循環学会誌
• 作者: Kageyama Hiroki;Osada Shohichi;Nakata Hiroyuki;Kubota Mitsuhiro;Matsuda Hitoki;景山広樹,長田昭一,窪田光宏,松田仁樹;景山広樹，長田昭一，窪田光宏，松田仁樹
• 通讯作者: 景山広樹，長田昭一，窪田光宏，松田仁樹

Effect of Coexisting Inorganic Chlorides on Lead Volatilization from CaO-SiO_2-Al_2O_3 Molten Slag under Municipal Solid Waste Gasification-Melting Conditions

城市生活垃圾气化熔融条件下共存无机氯化物对CaO-SiO_2-Al_2O_3熔渣中铅挥发的影响

• 发表时间: 2013
• 期刊: Fuel
• 影响因子: 7.4
• 作者: Kageyama Hiroki;Osada Shohichi;Nakata Hiroyuki;Kubota Mitsuhiro;Matsuda Hitoki
• 通讯作者: Matsuda Hitoki

Volatilization of lead compounds from CaO-SiO2-Al2O3 molten slag in different gas atmospheres

不同气氛下CaO-SiO2-Al2O3熔渣中铅化合物的挥发

• 作者: H. Matsuda;H. Kageyama;Y. Kawaguchi;S. Osada;M. Kubota
• 通讯作者: M. Kubota

都市ごみ溶融を模擬したCaO-SiO_2-Al_2O_3系溶融スラグからの酸化鉛の揮発速度解析の検討

模拟城市垃圾熔化CaO-SiO_2-Al_2O_3熔渣中氧化铅挥发率分析研究

• 发表时间: 2011
• 期刊: 廃棄物資源循環学会誌
• 作者: Kageyama;H.;S.Osada;H.Nakata;M.Kubota;H.Matsuda;景山広樹,河内山拓哉,長田昭一,河口祐輝,窪田光宏,松田仁樹
• 通讯作者: 景山広樹,河内山拓哉,長田昭一,河口祐輝,窪田光宏,松田仁樹