Experimental study of Irradiation Assisted Stress Corrosion Cracking by using Cyclotron Accelerator

回旋加速器辐照辅助应力腐蚀开裂实验研究

• 批准号: 22560830
• 负责人: MURASE Yoshiharu
• 金额: $ 1.75万
• 依托单位: National Institute for Materials Science
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22560830/
• 关键词: 原子力材料; 照射下疲労; 軽イオン照射; 水素脆化; ヘリウム予注入; 照射誘起応力腐食割れ; 軽水炉構造材料; サイクロトロン; その場試験; 水素効果; プロトン照射; 疲労; ヘリウム注入; 「その場」試験; 水素脆性; 重水素照射

The extension of fatigue lifetime under high-energy particle irradiation is considered as the in-situ irradiation effect based on the interaction between the radiation induced defect clusters and moving dislocations. The present experimental study was successful to demonstrate the reduction of the in-situ irradiation effect when hydrogen and helium are sufficiently included in the material. This indicates hydrogen would influence the irradiation assisted stress corrosion cracking (IASCC) for aging light-water-plant materials accumulating substantial amount of helium.

高能粒子辐照下疲劳寿命的延长被认为是基于辐照诱导的缺陷簇与运动位错之间的相互作用而产生的原位辐照效应。目前的实验研究成功地证明了当材料中含有足够的氢和氦时，原位辐照效应降低。这表明，氢将影响大量积累氦的轻水植物材料的辐照辅助应力腐蚀开裂(IASCC)。

项目成果

ヘリウム予注入した316鋼の17MeVプロトン照射下疲労挙動

17MeV质子辐照下预注氦316钢的疲劳行为

• 发表时间: 2011
• 作者: 村瀬義治;山本徳和;村瀬義治
• 通讯作者: 村瀬義治

Effects of implanted hydrogen on fatigue behavior of F82H under irradiation

• DOI: 10.1016/j.jnucmat.2010.12.049
• 发表时间: 2011-10
• 期刊: Journal of Nuclear Materials
• 影响因子: 3.1
• 作者: Y. Murase;J. Nagakawa;N. Yamamoto

Effects of Implanted Deuterium on In-Situ Irradiation Fatigue Behavoirs of Cold-Worked 316 Stainless Steel at 60 and 300℃

注入氘对冷加工316不锈钢60和300℃原位辐照疲劳行为的影响

• 发表时间: 2011
• 期刊: Materials Transactions
• 影响因子: 1.2
• 作者: 村瀬義治;山本徳和
• 通讯作者: 山本徳和