Application of the percolation model in the fracture phenomenon of wood

渗流模型在木材断裂现象中的应用

• 批准号: 22580185
• 负责人: NAKAI Takahisa
• 金额: $ 2.66万
• 依托单位: Shimane University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22580185/
• 关键词: 木材; 抄き紙; 破壊; パーコレーション; 生物物理; 物性実験; モデル化

About wood and paper yarn, the static fracture phenomenon was solved using percolation. In the model, the fracture phenomenon was clarified by catching a fracture phenomenon probabilistically, introducing the concept of the dangerous element based on local material strength, and describing the damage accumulative process and fracture intensity in static destruction in Monte Carlo simulation. As a result, static destruction of wood and paper yarn discovered that the latter could be described by percolation.

对于木材和纸纱线，采用渗流法解决了静态断裂现象。该模型通过概率性地捕捉断裂现象，引入基于局部材料强度的危险单元概念，并在Monte Carlo模拟中描述静态破坏时的损伤累积过程和断裂强度，从而阐明了断裂现象。结果，木材和纸纱线的静态破坏发现，后者可以用渗透来描述。

项目成果

Mechanical interaction between cellulose microfibrils and matrix substances in wood cell walls induced by repeated wet-and-dry treatment

反复干湿处理诱导纤维素微纤维与木材细胞壁基质物质之间的机械相互作用

• 发表时间: 2012
• 期刊: Cellulose
• 影响因子: 5.7
• 作者: Toba K;Yamamoto;H.;Yoshida;M
• 通讯作者: M

竹の形態形成と力学的構造構築との関係IV

竹子形态建成与机械结构构造的关系四

• 发表时间: 2012
• 作者: 安野恭代;中井毅尚;中田了五
• 通讯作者: 中田了五

Manufacture of a dental point with natural cellulose fibers

用天然纤维素纤维制造牙尖

• 发表时间: 2010
• 期刊: Transaction of MRS-J
• 作者: T. Nakai;K. Abe;G. Sekine;A. Yoshino
• 通讯作者: A. Yoshino

乾燥繰返し処理が引き起こした細胞壁セルロースの格子定数の変動

反复干燥处理引起细胞壁纤维素晶格常数的变化

• 发表时间: 2011
• 作者: 鳥羽景介;吉田正人;山本浩之;中井毅尚
• 通讯作者: 中井毅尚

乾湿繰返し処理によって起こる細胞壁セルロースの格子面間隔の変動

反复干湿处理引起细胞壁纤维素晶格间距的变化

• 发表时间: 2012
• 作者: 鳥羽景介;吉田正人;山本浩之
• 通讯作者: 山本浩之