Forming titanium oxide on low young's modulus titanium alloy by ECR plasma oxidation for developing biomechanical implant

ECR等离子体氧化在低杨氏模量钛合金上形成氧化钛用于开发生物力学植入物

• 批准号: 22791862
• 负责人: ORII Yusuke
• 金额: $ 2.58万
• 依托单位: Tohoku University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22791862/
• 关键词: インターフェイス; インプラント; チタン合金; 超弾性; 表面改質

After establishing the surface modification method of forming titanium oxide film on pure titanium surface by electron cyclotron resonance (ECR)plasma oxidation, we have achieved success in forming the same film on titanium alloy which young's modulus is close to human bone at various pressures and temperatures. Furthermore, cells culture showed that osteoblastic differentiation was also enhanced on this titanium dioxide film. It has the potential to become a surface modification method in improving the mechanical properties and biocompatibility of titanium alloy close to body bone tissue in implant-bone interface.

在建立了电子回旋共振（ECR）等离子体氧化在纯钛表面形成氧化钛膜的表面改性方法后，我们在不同压力和温度下成功地在杨氏模量接近人体骨的钛合金表面形成了同样的膜。此外，细胞培养显示，成骨细胞分化也在该二氧化钛膜上增强。该方法有望成为改善种植体-骨界面钛合金力学性能和生物相容性的一种表面改性方法。

项目成果

電子サイクロトロン共鳴プラズマ酸化による生体用金属材料Ti-Nb-Sn合金表面へのナノ構造付与

电子回旋共振等离子体氧化在生物金属材料Ti-Nb-Sn合金表面沉积纳米结构