Production of aluminum foam sandwich panel by melt drag process

熔体拖动法生产泡沫铝夹芯板

• 批准号: 22760103
• 负责人: NISHIDA Shinichi
• 金额: $ 1.25万
• 依托单位: Gunma University (2011)Waseda University (2010)
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22760103/
• 关键词: ポーラスアルミニウム; 発泡アルミニウム; ハニカムアルミニウム; メルトドラッグ法; サンドイッチパネル; 薄板連続鋳造法; アルミニウム合金; 軽量構造材料; 薄板連続鋳造; 接合

Production of aluminum foam sandwich panel and honeycomb sandwich panel was succeeded by melt drag process that was one of the strip casting processes. Suitable experimental conditions, bonding interface, bending stress and peeling stress were revealed. Commercial alloy A5052, A6063 and A7075 were adapted to this process.

采用薄带铸轧工艺中的熔体牵引法成功地生产了泡沫铝夹芯板和蜂窝夹芯板。揭示了合适的实验条件、键合界面、弯曲应力和剥离应力。商业合金A5052、A6063和A7075适用于该工艺。

项目成果

Producing Aluminum Honeycomb Sandwich Panel by Melt Drag Process

熔融拖动工艺生产铝蜂窝夹芯板

• 发表时间: 2012
• 作者: M. Okayasu;S. Takasu;S. Yoshie;西田進一
• 通讯作者: 西田進一

Producing Aluminum Foam Sandwich Panel by Melt Drag Process

熔融拖动工艺生产泡沫铝夹芯板

• 发表时间: 2012
• 期刊: Materials Science Forum
• 作者: 西田進一;田中寛人;安達眞人;本村貢
• 通讯作者: 本村貢

メルトドラッグ法による発泡アルミサンドイッチパネルの作製による被覆合金薄肉化と拡散接合による高接合強度化

采用熔拖法制作泡沫铝夹芯板，使涂层合金变薄，并通过扩散结合增加结合强度

• 发表时间: 2010
• 作者: 田中寛人;浅川史章;大木純;西田進一;本村貢
• 通讯作者: 本村貢