Molecular weight effects on structural formation of polymers under shear flow

剪切流下分子量对聚合物结构形成的影响

• 批准号: 22750197
• 负责人: MATSUBA Go
• 金额: $ 2.66万
• 依托单位: Yamagata University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22750197/
• 关键词: 高分子材料物性; ナノ構造; 繊維材料; 高分子物性; ポリエチレン; 結晶化; 量子ビーム; 高分子結晶; 繊維構造; 散乱法

In order to clarify the shish-kebab formation process, we carried out the quantum beam analysis and FT-IR measurements. Especially, the effects of molecular weight on the shish-kebabs and conformational changes were focused on. By neutron and synchrotron radiation x-ray scattering measurements, we observed the oriented structure of low molecular weight component with about 1 micron. From FT-IR measurements, we succeeded the conformation of precursors, which has crystalline conformations.

为了阐明烤肉串的形成过程，我们进行了量子束分析和傅立叶变换红外测量。特别关注了分子量对烤羊肉串的影响和构象变化。通过中子和同步加速器辐射X射线散射测量，我们观察到了约1微米的低分子量组分的取向结构。通过 FT-IR 测量，我们成功确定了前体的构象，它具有结晶构象。

项目成果

大学

大学

Shear-induced crystallization and rheological behavior of syndiotactic polystyrene

间规聚苯乙烯的剪切诱导结晶和流变行为

• 发表时间: 2012
• 期刊: J. Mater. Res
• 作者: Zhao Y;Matsuba G;Ito H
• 通讯作者: Ito H

高分子の結晶化メカニズムと精密構造解析

聚合物结晶机理和精确结构分析

• 发表时间: 2011
• 作者: Matsuba G;Tomita N;Hanano S;Nishida K;Kanaya T;Aoi Inomata;Matsuba Go;酒井 康博;Matsuba Go;松葉豪
• 通讯作者: 松葉豪

Fiber structure analysis in a wide spatial scale with a quantum beam

使用量子束进行宽空间尺度的纤维结构分析

• 发表时间: 2011
• 作者: Aoi Inomata;Masatoshi Kidowaki;Yasuhiro Sakai;Hideaki Yokoyama and Kohzo Ito;Matsuba Go
• 通讯作者: Matsuba Go

The precise analysis for shish-kebab formation processes and melting

烤肉串形成过程和熔化的精确分析

• 发表时间: 2011
• 作者: Matsuba G;Tomita N;Hanano S;Nishida K;Kanaya T;Aoi Inomata;Matsuba Go;酒井 康博;Matsuba Go
• 通讯作者: Matsuba Go