To prevent a sharp rise in load in compression of plates, a compression process using load pulsation was developed. The mechanism of the load pulsation was investigated. The load pulsation was applied for backward extrusion, flange forming and bulk forming of stainless steel sheet. The forming load was decreased and accuracy of the formed shape was increased by the load pulsation.

为了防止在板的压缩中载荷的急剧上升，开发了使用载荷脉动的压缩过程。研究了负载脉动的机理。对不锈钢板的反挤压、凸缘成形和体积成形进行了载荷脉动试验。通过载荷脉动，减小了成形载荷，提高了成形形状的精度。

项目成果

ほか,板鍛造における荷重振動を用いたステンレス鋼部品の段差付け加工

另外，在板材锻造中利用载荷振动对不锈钢零件进行分步加工

• 发表时间: 2011
• 作者: T. Maeno;K. Osakada;K. Mori;前野智美;前野智美;前野智美;前野智美
• 通讯作者: 前野智美

Reduction of friction in compression of plates by load pulsation

• DOI: 10.1016/j.ijmachtools.2011.03.007
• 发表时间: 2011-07-01
• 期刊: INTERNATIONAL JOURNAL OF MACHINE TOOLS & MANUFACTURE
• 影响因子: 14
• 作者: Maeno, T.;Osakada, K.;Mori, K.
• 通讯作者: Mori, K.

サーボプレスを用いた摩擦を低減する荷重振動鍛造

使用伺服压力机进行负载振动锻造以减少摩擦

• 发表时间: 2011
• 作者: T. Maeno;K. Osakada;K. Mori;前野智美
• 通讯作者: 前野智美

板鍛造における荷重振動を用いたステンレス鋼部品の段差付け加工

板锻中利用载荷振动对不锈钢零件进行阶梯加工

• 发表时间: 2011
• 作者: 前野智美;ほか
• 通讯作者: ほか