High-Efficiency Technology of Iron Carburization using Biomass char by which carbon crystallinity is controlled.

利用生物质炭控制碳结晶度的高效铁渗碳技术。

• 批准号: 22760577
• 负责人: OHNO Ko-ichiro
• 金额: $ 2.58万
• 依托单位: Kyushu University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22760577/
• 关键词: 省エネプロセス; バイオマス; 浸炭; 溶融; 炭素結晶性; 製鉄; ラマン分光分析; 灰分

Charcoal use instead of fossil fuel is one of the possible technologies for mitigation of CO2 emission in the steel industry because charcoal can be considered as“carbon-neutral"material. In this study, the possibility of utilization of charcoal as carbon source for carburization reaction was examined ; more specifically effects of carbon crystalinity and ash in charcoal on carbon dissolution into molten iron and iron carburization reaction in iron-charcoal composite were investigated. From these investigations, following results were revealed. Charcoal heat-treated at low temperature, 1273K, has advantage for carbon dissolution reaction into iron bath. Charcoal ash strongly prevents the carburization reaction between iron and carbon.

由于木炭是一种“碳中性“材料，因此使用木炭替代化石燃料是钢铁行业减少CO2排放的可能技术之一。本研究探讨了利用木炭作为渗碳反应碳源的可能性，研究了木炭中碳的结晶度和灰分对铁炭复合材料中碳溶解和铁渗碳反应的影响。从这些调查中，揭示了以下结果。在1273K低温下热处理的木炭有利于碳在铁浴中的溶解反应。木炭灰强烈地阻止铁和碳之间的渗碳反应。

项目成果

High-Efficiency Technology of Iron Carburization by TabletFe(l) Fe(l) Fe(l) 1131. 21166. 71188. 71244. 9352. 8 mm352. 8 mm352. 8 mm352. 8 mm using Biomass char in Ironmaking Process

铁片高效渗碳技术Fe(l) Fe(l) Fe(l) 1131. 21166. 71188. 71244. 9352. 8 mm352.

• 发表时间: 2011
• 作者: Alexander Babich;Pruet Kowitwarangkul;Dieter Senk;Heinrich Wilhelm Gudenau;Ko-ichiro Ohno;Masakata Shimizu;Yasuaki Ueki;Ko-ichiro Ohno
• 通讯作者: Ko-ichiro Ohno

廃棄物の製鉄利用を目指した鉄-水素コプロダクションシステム

钢氢联产系统旨在利用废物进行钢铁生产

• 发表时间: 2011
• 期刊: 化学工学
• 作者: 大野光一郎;清水正賢
• 通讯作者: 清水正賢

Dieter SENK, Heinrich Wilhelm GUDENAU and Masakata SHIMIZU, Effects of Charcoal Carbon Crystallinity and Ash Content on Carbon Dissolution in Molten Iron and Carburization Reaction in Iron-Charcoal Composite

Dieter SENK、Heinrich Wilhelm GUDENAU 和 Masakata SHIMIZU，木炭碳结晶度和灰分含量对铁水碳溶解和铁炭复合材料渗碳反应的影响

• 发表时间: 2012
• 期刊: ISIJ International
• 影响因子: 1.8
• 作者: Ko-ichiro OHNO;Alexander BABICH;Junki MITSUE;Takayuki MAEDA
• 通讯作者: Takayuki MAEDA

Use of charcoal, biomass and waste plastics for reducing CO2 emission in ironmaking

利用木炭、生物质和废塑料减少炼铁过程中的二氧化碳排放

• 发表时间: 2011
• 期刊: Proceedings of 1st International Conference on Energy Efficiency and CO2 Reduction in the Steel Industry
• 作者: Alexander Babich;Pruet Kowitwarangkul;Dieter Senk;Heinrich Wilhelm Gudenau;Ko-ichiro Ohno;Masakata Shimizu;Yasuaki Ueki
• 通讯作者: Yasuaki Ueki

高炉炉床溶銑流の炭素溶解度変化による耐火物の溶損特性

高炉炉底铁水流中碳溶解度变化对耐火材料的侵蚀特性

• 发表时间: 2011
• 期刊: 材料プロセス
• 作者: 白石祐規;三枝純己;大野光一郎;前田敬之;清水正賢;西岡浩樹
• 通讯作者: 西岡浩樹