In this study, we have developed two surface modifications of titanium alloy that improves its biofunctional activity. The surface of a Ti-6Al-4V disk was modified by applying 3% H2O2 hydrothermal treatment using an autoclave. A nanostructured porous network TiO2 was observed on the treated surface. Furthermore, the TiO2 titan disks were immersed in the supersaturated calcium phosphate solution to formed nano-apatite layer. We evaluated the surface analysis and bioactivities for FGF2 coated modified surfaces. As the results, significantly higher cell proliferation and celldifferentiation were exhibited, and enhanced biofunctional activity.

在这项研究中，我们开发了两种钛合金表面改性，以提高其生物功能活性。使用高压釜采用 3% H2O2 水热处理对 Ti-6Al-4V 圆盘进行表面改性。在处理过的表面上观察到纳米结构的多孔网络 TiO2。此外，将TiO2钛盘浸入过饱和磷酸钙溶液中以形成纳米磷灰石层。我们评估了 FGF2 涂层改性表面的表面分析和生物活性。结果，显示出显着更高的细胞增殖和细胞分化，并增强了生物功能活性。

项目成果

他過酸化水素水を用いた水熱処理による酸化チタン膜の形成とその表面解析

双氧水水热处理氧化钛薄膜的形成及其表面分析

• 发表时间: 2011
• 作者: Hasegawa T;et al;斎藤沙耶;斎藤沙耶;長谷川智一;斎藤沙耶;斉藤沙耶;斉藤沙耶;斉藤沙耶;松野智宣;米山勇哉
• 通讯作者: 米山勇哉

他bFGF2含浸HA矯正用ミニスクリューの生体親和性の検討

检查其他 bFGF2 浸渍迷你螺钉用于 HA 矫正的生物相容性

• 发表时间: 2012
• 作者: Hasegawa T;et al;斎藤沙耶;斎藤沙耶;長谷川智一;斎藤沙耶
• 通讯作者: 斎藤沙耶

他Bioactiveに機能する矯正用ミニスクリューの開発

开发可与其他生物活性材料配合使用的正畸微型螺钉

• 发表时间: 2012
• 作者: Hasegawa T;et al;斎藤沙耶
• 通讯作者: 斎藤沙耶

他HA/FGF2処理によるチタン表面のbioactivityの評価

其他 HA/FGF2 处理对钛表面生物活性的评价

• 发表时间: 2012
• 作者: Hasegawa T;et al;斎藤沙耶;斎藤沙耶
• 通讯作者: 斎藤沙耶

Bioactiveに機能する矯正用ミニスクリューの開発

开发具有生物活性的正畸微型螺钉

• 发表时间: 2012
• 作者: Hasegawa T;et al;斎藤沙耶;斎藤沙耶;長谷川智一;斎藤沙耶;斉藤沙耶
• 通讯作者: 斉藤沙耶