The proposal for the next-generation microstructural control technique of steel by using ultra-fine lath austenitic starting structure

采用超细板条奥氏体起始组织的下一代钢显微组织控制技术的建议

• 批准号: 22686065
• 负责人: NAKADA Nobuo
• 金额: $ 12.31万
• 依托单位: Kyushu University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (A)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22686065/
• 关键词: 鉄鋼材料; 超微細粒; 相変態; 組織制御; マルテンサイト変態

For the production of fine-grained structural steel, the microstructural characteristics of lath austenite formed by martensitic reversion and the microstructure transformed from it were investigated. As a result, it was confirmed in a model steel that the lath austenite has fine lath structure containing high-density dislocations. In addition, it was suggested that martensitic reversion takes place even in a low alloyed steel under the specific condition controlled by alloy designing and heat treatment.

为了生产细晶结构钢，研究了马氏体逆转变板条奥氏体的组织特征及其转变组织。结果，在模型钢中确认了板条奥氏体具有包含高密度位错的微细板条结构。此外，还指出，在合金设计和热处理控制的特定条件下，即使是低合金钢也会发生马氏体回复。

项目成果

せん断型逆変態により生成したオーステナイト組織の特徴

剪切型逆相变生成奥氏体组织的特征

• 发表时间: 2011
• 作者: Fumio Kawamura;Takashi Taniguchi;中田伸生
• 通讯作者: 中田伸生

せん断型逆変態により形成されるオーステナイト組織

剪切型逆相变形成奥氏体组织

• 发表时间: 2012
• 作者: 深川怜史;中田伸生;土山聡宏;高木節雄
• 通讯作者: 高木節雄