Study on cut-edge corrosion mechanism of galvanized corrosion and improvement of corrosion resistance by utilizing multiphysics analysis

利用多物理场分析研究镀锌腐蚀的前沿腐蚀机理并提高耐蚀性

• 批准号: 23560861
• 负责人: TADA EIJI
• 金额: $ 3.49万
• 依托单位: Tokyo Institute of Technology
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011 至 2013
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23560861/
• 关键词: 電位分布; 電流分布; イオン分布; 腐食生成物; ガルバニ腐食; マイクロ電気化学; 数値シミュレーション; カソード反応; 数値シュミレーション

This study focused on cut-edge corrosion mechanism of galvanized steels. In order to investigate anodic and cathodic reactions on steels with Zn corrosion products formed in 1 M NaCl and 1 M MgCl2, electrochemical microcell technique was employed. The morphology and compositions of Zn corrosion products formed on the steels depended on solution compositions and the distance from zinc coating layer. In addition, cathodic reaction was suppressed to some extent by deposition of the corrosion products. On the other hand, anodic reaction was suppressed on steel significantly by precipitation of the corrosion products containing Mg.

本文主要研究了镀锌钢的刃口腐蚀机理。为了研究锌在1M氯化钠和1M氯化镁中形成的腐蚀产物在钢上的阳极和阴极反应，采用了电化学微电池技术。在钢表面形成的锌腐蚀产物的形态和组成与溶液组成和与镀锌层的距离有关。此外，腐蚀产物的沉积在一定程度上抑制了阴极反应。另一方面，含镁腐蚀产物的析出显著抑制了钢的阳极反应。

项目成果

亜鉛の腐食生成物が堆積した鋼板上における酸素還元反応特性の評価

沉积有锌腐蚀产物的钢板上氧还原反应特性的评价

• 发表时间: 2013
• 作者: 片上慎也;多田英司;西方篤
• 通讯作者: 西方篤

亜鉛の腐食生成物が堆積した鋼板上におけるアノード反応特性

沉积锌腐蚀产物钢板的阳极反应特性

• 发表时间: 2014
• 作者: 片上慎也;多田英司;西方篤
• 通讯作者: 西方篤