Preparation of "Janus"-type Nanosheets

“Janus”型纳米片的制备

• 批准号: 23655205
• 负责人: SUGAHARA Yoshiyuki
• 金额: $ 2.58万
• 依托单位: Waseda University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Challenging Exploratory Research
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23655205/
• 关键词: 層状; 層間化合物; ナノシート; 層状ニオブ酸塩; 有機ホスホン酸; グラフト反応; 有機誘導体; “ヤヌス”型; インターカレーション; 層状六ニオブ酸

K_4Nb_6O_<17>・3H_2O ion-exchanged with (C_<18>H_<37>)_2N(CH_3)_2+ ions were reacted with phenylphosphonic acid to prepare a A-type derivative possessing modified an interlayer I. Then, C_<12>H_<25>NH_3+ ions were introduced into an unmodified interlayer II and a resulting intermediate was further treated with carboxyalkylphosphonic acids (COOHCnP;n=1-3). The nanosheets in the products were likely to possess two interlayer surfaces modified with different organophosphonate moieties.

用<17>（C_<18>H_<37>）_2N（CH_3）_2+离子交换的K_4Nb_6O_ ·3H_2O与苯基膦酸反应，制备了具有改性中间层I的A型衍生物。然后将C_<12>H_<25>NH_3+离子引入未改性的中间层II中，并将所得中间体进一步用羧基烷基膦酸（COOHCH 3;n=1-3）处理。产物中的纳米片可能具有两个用不同有机膦酸酯部分改性的层间表面。

项目成果

フェニルホスホン酸の層表面修飾による層状ニオブ酸塩K_4Nb_6O_<17> のA-type 及びB-type 有機誘導体の合成

苯基膦酸层状表面修饰合成层状铌酸盐K_4Nb_6O_<17>A型和B型有机衍生物

• 发表时间: 2012
• 作者: 佐藤久子;田村堅志;山岸晧彦;小池信太郎，馬場正和，中村航太郎，K.M. Ajamal，Weijie Du，都甲薫，末益崇;鈴木涼子,長浜慎太郎,加藤由実,島田亮,菅原義之
• 通讯作者: 鈴木涼子,長浜慎太郎,加藤由実,島田亮,菅原義之

フェニルホスホン酸の層表面修飾による層状ニオブ酸塩K4Nb6O17のA-type及びB-type有機誘導体の合成

苯基膦酸层状表面修饰合成层状铌酸盐K4Nb6O17 A型和B型有机衍生物

• 作者: 佐藤久子;森本和也;小田切健;田村堅志;鈴木涼子
• 通讯作者: 鈴木涼子