Synthesis of novel acceptor type graphite intercalation compounds and its superconductivity

新型受主型石墨插层化合物的合成及其超导性能

基本信息

批准号：
23655203
负责人：
TOYODA Masahiro
金额：
$ 2.5万
依托单位：
Oita University
依托单位国家：
日本
项目类别：
Grant-in-Aid for Challenging Exploratory Research
财政年份：
2011
资助国家：
日本
起止时间：
2011 至 2013
项目状态：
已结题

项目摘要

Synthesis of S-GIC (graphite intercalation compounds) was carried out by soaking the graphite sheet (GS) and Exfoliated graphite sheets (ExGS) which is the host materials in the sulfur which melted at 350 oC for 24 h under air atmosphere. New peaks which did not correspond to host materials or the sulfur which is intercalated was able to confirm it on XRD pattern. Formation of the intercalation compounds were indicated. However, in the case of synthesis of S-GIC under inert atmosphere such as N2, it was not carried out in the same conditions. The confirmation of new peaks recognized in the synthesis in the air was not possible in it.

S-GIC（石墨插层化合物）的合成是将石墨片（GS）和膨胀石墨片（ExGS）作为主体材料，在空气气氛下在350℃熔化的硫磺中浸泡24小时。与主体材料或插入的硫不对应的新峰能够在 XRD 图案上证实。表明了插层化合物的形成。然而，在惰性气氛如N 2 下合成S-GIC时，并不是在相同的条件下进行的。在空气中合成中识别出的新峰的确认在其中是不可能的。

项目成果

期刊论文数量（0）

专著数量（0）

科研奖励数量（0）

会议论文数量（0）

专利数量（0）

電気化学的手法を用いた黒鉛材料へのドナータイプのインターカレーション挙動

使用电化学方法研究石墨材料中供体类型的插层行为

DOI：
发表时间：
2013
期刊：
影响因子：
0
作者：
中村昴;衣本太郎;津村朋樹;豊田昌宏
通讯作者：
豊田昌宏

アルカリ土類金属の膨張黒鉛へのインターカレーション

碱土金属嵌入膨胀石墨中

DOI：
发表时间：
2012
期刊：
影响因子：
0
作者：
Y. Ouchi;S. Ueda;A. Takenaka;T. Kinumoto;T. Tsumura;M. Toyoda;磯野拓也;上田悟司，衣本太郎，津村朋樹，豊田昌宏;大塚一世;中村昴，衣本太郎，津村朋樹，豊田昌宏
通讯作者：
中村昴，衣本太郎，津村朋樹，豊田昌宏

H.Kamimura, Phys. Today , 4 0 Vol.40, No.12 (1987) 64-71.(参考文献)

H.Kamimura，《今日物理学》，4 0 Vol.40，No.12 (1987) 64-71。（参考文献）