Influence of light intensity on polymerization rate of spectral distribution

光强对光谱分布聚合率的影响

• 批准号: 23792194
• 负责人: IROKAWA Atsushi
• 金额: $ 1.58万
• 依托单位: Nihon University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23792194/
• 关键词: LED 照射器; 光重合型レジン; 照射特性; 可視光線照射器; 重合収縮; 照射器; LED; ヌープ硬さ

The influence of halogen and LED curing unit on the mechanical properties of resin composite was investigated. Halogen units had a spectral peak at 480nm, while LED units had peaks from 453-465nm. Significant differences were observed in depth of polymerization, polymerization shrinkage, knoop hardness. The results of this study suggest that the type of curing unit influences mechanical properties of resin composite.

研究了卤素和LED固化单元对树脂复合材料力学性能的影响。卤素单元在480 nm处具有光谱峰，而LED单元在453- 465 nm处具有峰。在聚合深度、聚合收缩率、努氏硬度方面观察到显著差异。研究结果表明，固化单元的类型影响树脂复合材料的力学性能。

项目成果

照射器光線の光強度が新規修復システムの象牙質接着性に及ぼす影響

照射光束光强对新型修复系统牙本质粘附的影响

• 发表时间: 2012
• 期刊: 接着歯学
• 作者: Washio A;Kitamura C;Morotomi T;Terashita M;Nishihara T;野尻貴絵，辻本暁正，坪田圭司，陸田明智，安藤 進，宮崎真至;鷲尾絢子，平田志津，市丸美希，西藤法子，北村知昭;黒川弘康，宮崎真至
• 通讯作者: 黒川弘康，宮崎真至

試作知覚過敏抑制材の象牙細管封鎖性に関する研究 超音波透過法を用いた検討

原型过敏抑制材料的牙本质小管封闭性能研究：超声传输法研究

• 作者: 色川敦士;高見澤俊樹;坪田圭司;森健太郎;山本明;古市哲也;横川未穂;高橋史典;黒川弘康;宮崎真至;黒川 弘康;色川敦士;清水裕亮;色川敦士;高見澤俊樹;高見澤俊樹;高見澤俊樹;遠藤肇;遠藤肇;古宅眞由美;山本明;高見澤俊樹;瀧本正行;山本明;高見澤俊樹;遠藤 肇
• 通讯作者: 遠藤 肇

コンポジットレジンの機械的性質および臨床応用

复合树脂的力学性能及临床应用

• 发表时间: 2012
• 作者: 色川敦士;高見澤俊樹;坪田圭司;森健太郎;山本明;古市哲也;横川未穂;高橋史典;黒川弘康;宮崎真至;黒川 弘康;色川敦士;清水裕亮;色川敦士;高見澤俊樹
• 通讯作者: 高見澤俊樹

表面自由エネルギーからのコア用レジンの歯質接着性の検討

从表面自由能检查核心树脂对牙齿结构的粘附力

• 发表时间: 2012
• 作者: Murayama R;Miyazaki M;清水裕亮
• 通讯作者: 清水裕亮

仮着材の残留が自己接着性セメントの象牙質接着性に及ぼす影響

残留临时粘合剂对自粘水门汀牙本质粘合力的影响

• 发表时间: 2011
• 作者: 色川敦士;高見澤俊樹;坪田圭司;森健太郎;山本明;古市哲也;横川未穂;高橋史典;黒川弘康;宮崎真至;黒川 弘康;色川敦士;清水裕亮;色川敦士;高見澤俊樹;高見澤俊樹;高見澤俊樹;遠藤肇;遠藤肇;古宅眞由美;山本明;高見澤俊樹;瀧本正行
• 通讯作者: 瀧本正行