Phonon Analysis on Ion Conductive Oxides Using Broadband Conductivity Spectroscopy

使用宽带电导率谱对离子导电氧化物进行声子分析

• 批准号: 23750242
• 负责人: TERANISHI Takashi
• 金额: $ 2.83万
• 依托单位: Okayama University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23750242/
• 关键词: 酸化物イオン伝導体; 広帯域導電スペクトル法; 定化ジルコニア; バルク導電率; 格子振動パラメータ; 安定化ジルコニア; イオン伝導体; イオンホッピング; 格子振動

The evaluation technique that provides a broadband conductivity spectra from low to THz frequencies for oxygen ion conductor ceramics was developed in this study. The relationship between the optical phonon behavior and the ion conductivity was quantitatively investigated by applying this technique to some oxygen ion conductors(ex. yttria-stabilized zirconia). As a result, the existence of the relation between these parameters; smaller damping factor of the optical vibration leads to higher ion conductivity, was found.

本研究发展了氧离子导体陶瓷从低频到太赫兹频段的宽带导电谱评价技术。将该技术应用于某些氧离子导体，定量研究了光学声子行为与离子电导率之间的关系。氧化钇稳定的氧化锆)。结果发现，这些参数之间存在一定的关系，光学振动的衰减因子越小，离子电导率越高。

项目成果

広帯域導電率測定によるZrO2系酸化物イオン伝導体の電気伝導挙動の解析

宽带电导率测量分析ZrO2基氧化物离子导体的导电行为

• 发表时间: 2012
• 作者: 寺西 貴志

ZrO2基イオン伝導体セラミックスにおける準ミリ波吸収挙動の解析

ZrO2基离子导体陶瓷准毫米波吸收行为分析

• 发表时间: 2012
• 作者: 寺西貴志，秋山 直毅，綾野 敬子，林秀考，岸本昭

Broadband Conductivity Spectroscopy on Zirconia-based Ion Conductors

氧化锆基离子导体的宽带电导率光谱

• 发表时间: 2011
• 作者: T. Teranishi;K. Shimizu;H. Hayashi;and A. Kishimoto
• 通讯作者: and A. Kishimoto

Analysis of Conduction Behavior in ZrO2-based Ceramics using Broadband Conductivity Spectroscopy

使用宽带电导率光谱分析 ZrO2 基陶瓷的导电行为

• 发表时间: 2012
• 作者: Y. Asada;K. Miyazaki;T. Fukutsuka;and T. Abe;Takashi Teranishi
• 通讯作者: Takashi Teranishi

酸化物イオン伝導体M2O3-ZrO2(M = Al, Gd, Y, Yb)における広帯域複素導電率

氧化物离子导体 M2O3-ZrO2 中的宽带复电导率（M = Al、Gd、Y、Yb）

• 发表时间: 2012
• 作者: 田港聡,平山雅章,Yueming Zheng;鈴木耕太,Kyungsu Kim,粉生守,南嶋宏映,菅野了次,孫珍永,田村和久,水木純一郎;寺西 貴志
• 通讯作者: 寺西 貴志