Elucidation of gigacycle fatigue mechanism of high-strength steel using a nano beach mark method

利用纳米滩标法阐明高强钢的千兆循环疲劳机理

• 批准号: 23760106
• 负责人: FURUYA Yoshiyuki
• 金额: $ 2.83万
• 依托单位: National Institute for Materials Science
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23760106/
• 关键词: 疲労; ギガサイクル疲労; 高強度鋼; 内部破壊; 介在物

The internal fatigue crack growth was successfully visualized by using beach marks, which is necessary for the elucidation of gigacycle fatigue mechanism of high-strength steel. The beach marks indicated that a minimum crack propagation rate could be smaller than a lattice length. This means that evaluation of the gigacycle fatigue strength could be based on the crack propagation life.

利用海滩标记成功地显示了高强度钢的内部疲劳裂纹扩展过程，这对阐明高强度钢的疲劳机制是必要的。海滩标记指示最小裂纹扩展速率可小于晶格长度。这意味着可以基于裂纹扩展寿命来评估千兆赫疲劳强度。

项目成果

SCM440 鋼ダブルメルト材のギガサイクル疲労特性

SCM440钢双熔体材料的千兆周疲劳性能

• 发表时间: 2012
• 作者: Hama;T.,Seto;Y.;Tanaka;M.;Kusano;H.;Hirano;Y.;Aoki;Y.;Saito;H.;Kimpara;I.;白田竜也;Shinichi Enoki;坂田誠一郎;田中 展，泉 聡志，酒井 信介;古谷佳之
• 通讯作者: 古谷佳之

Gigacycle Fatigue Properties of Double-Melted SCM440 Steel and Size Effects

双熔SCM440钢的十亿周疲劳性能及尺寸效应

• DOI: 10.2355/tetsutohagane.99.373
• 发表时间: 2013
• 期刊: Tetsu-to-Hagane
• 作者: 櫻井香織;熊谷進;古谷佳之
• 通讯作者: 古谷佳之

高清浄度鋼のギガサイクル疲労における寸法効果

尺寸对高洁净度钢千兆循环疲劳的影响

• 发表时间: 2012
• 作者: 永倉知,田中和人,片山傳生;田中基嗣;古谷佳之
• 通讯作者: 古谷佳之