Fabrication of functionally graded porous aluminum and its deformation behavior estimation by image-based analysis

功能梯度多孔铝的制造及其基于图像分析的变形行为估计

• 批准号: 23760649
• 负责人: HANGAI Yoshihiko
• 金额: $ 2.83万
• 依托单位: Gunma University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23760649/
• 关键词: ポーラスアルミニウム; 傾斜機能材料; ポーラス金属; 多孔質金属; 発泡金属; 摩擦攪拌; 傾斜機能; ダイカスト; 摩擦攪拌接合; イメージベース解析; Ｘ線ＣＴ

Functionally graded (FG) aluminum foam containing A1050 pure aluminum and ADC12 aluminum alloy was fabricated. The FG foam has the potential for its location of deformation to be controlled. Moreover, a FG foam with plateau regions and stresses corresponding to those of the uniform A1050 and ADC12 foams was obtained. Also, we performed image-based finite element (FE) analyses of FG aluminum foam using X-ray computed tomography (CT) images and investigated the possibility of predicting its deformation behavior by comparing the results of FE analyses with those of actual compressive tests.

制备了以A1050纯铝和ADC 12铝合金为主要成分的功能梯度泡沫铝。FG泡沫具有控制其变形位置的潜力。此外，获得了具有平台区域和对应于均匀A1050和ADC 12泡沫的应力的FG泡沫。此外，我们进行了基于图像的有限元（FE）分析FG泡沫铝使用X射线计算机断层扫描（CT）图像和研究预测其变形行为的可能性，通过比较有限元分析的结果与实际的压缩试验。

项目成果

Compression properties of Al/Al-Si-Cu alloy functionally graded aluminum foam fabricated by friction stir processing route

• DOI: 10.2320/matertrans.m2012376
• 发表时间: 2013-03
• 期刊: Materials Transactions
• 影响因子: 1.2
• 作者: Y. Hangai;Kousuke Saito;T. Utsunomiya;Soichiro Kitahara;O. Kuwazuru;N. Yoshikawa

Osamu Kuwazuru and Nobuhiro Yoshikawa, Nondestructive observation of pore structure deformation behavior of functionally graded aluminum foam by X-ray computed tomography

Osamu Kuwazuru 和 Nobuhiro Yoshikawa，功能梯度泡沫铝孔结构变形行为的 X 射线计算机断层扫描无损观察

• 发表时间: 2012
• 期刊: Materials Science & Engineering A
• 作者: Yoshihiko Hangai;Kazuya Takahashi;Ryo Yamaguchi;Takao Utsunomiya;Soichiro Kitahara
• 通讯作者: Soichiro Kitahara

X線CTイメージベースFEMによるポーラスアルミニウムの傾斜機能化の有効性評価

使用基于 X 射线 CT 图像的 FEM 评估功能梯度多孔铝的有效性

• 发表时间: 2013
• 期刊: 日本機械学会論文集A編
• 作者: Hajime Nagata;K. Tabuchi;N. Yawata and Tadashi Takenaka;木皿自然;山口亮,吉田浩亮,半谷禎彦,桑水流理,吉川暢宏
• 通讯作者: 山口亮,吉田浩亮,半谷禎彦,桑水流理,吉川暢宏

A1050-ADC12傾斜機能ポーラスアルミニウムの圧縮特性と気孔形態の評価

A1050-ADC12功能梯度多孔铝的压缩性能和孔形貌评价

• 发表时间: 2012
• 作者: Y. Yamazaki;M. Yoshimoto;O. Takeda;M. Kinsho; T. Taguchi;S. Yamamoto;T. Kurihara;I. Sugai;齋藤公佑
• 通讯作者: 齋藤公佑

異種合金による三層傾斜機能ポーラスアルミニウムの創製

使用不同合金创建三层功能梯度多孔铝

• 发表时间: 2013
• 期刊: 日本機械学会論文集A編
• 作者: T. Taguchi;N. Igawa;S. Shamoto;齋藤公佑,半谷禎彦,宇都宮登雄,桑水流理,吉川暢宏,北原総一郎
• 通讯作者: 齋藤公佑,半谷禎彦,宇都宮登雄,桑水流理,吉川暢宏,北原総一郎