Development of surface modification technique for ceramic reinforcements by metallic nanopartiles and the application to MMCs

金属纳米颗粒陶瓷增强材料表面改性技术的发展及其在MMCs中的应用

• 批准号: 23760708
• 负责人: MIZUMOTO Masayuki
• 金额: $ 2.91万
• 依托单位: Iwate University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23760708/
• 关键词: 金属ナノ粒子; 金属基複合材料; 自発溶浸法; 無電解めっき; 自発溶浸; 複合材料; 表面処理

Fabrication process of Cu and Ni nanoparticles by electroless plating method were developed. The size of the nanoparticles was controlled by controlling the plating conditions. When alumina particle reinforcements modified by Cu nanoparticles were heat-treated, the Cu nanoparticles were changed to CuO nanoparticles. Al alloy melt was infiltrated spontaneously into the alumina particle layer modified by CuO nanoparticles due to the thermite process resulting the improvement of the wettability between alumina and Al alloy melt. It is suggested that Cu nanopartiles having high specific surface area would be oxidized and reacted with Al alloy melt easily and resulted in the spontaneous infiltration.

研究了化学镀法制备纳米铜和纳米镍的工艺。通过控制镀覆条件来控制纳米颗粒的尺寸。经热处理后，Cu纳米粒子转变为CuO纳米粒子。铝合金熔体在铝热过程中自发地渗透到CuO纳米粒子改性的氧化铝粒子层中，从而改善了氧化铝与铝合金熔体之间的润湿性。结果表明，高比表面积的Cu纳米粒子易被氧化，与Al合金熔体发生反应，导致自发熔渗。

项目成果

Al合金基複合材料中の界面組織に及ぼすアルミナ繊維の影響

氧化铝纤维对铝合金基复合材料界面结构的影响

• 发表时间: 2011
• 作者: 平木岳人;長坂徹也;水本将之
• 通讯作者: 水本将之

メカニカルミリングによるAl_2O_3/Al複合材料の作製

机械铣削制备Al_2O_3/Al复合材料

• 发表时间: 2011
• 作者: Shunsuke Kashiwakura;Kazuaki Wagatsuma;水本将之
• 通讯作者: 水本将之

メカニカルミリングにより作製したAl_2O_3/Al複合材料の特性評価

机械铣削制备Al_2O_3/Al复合材料的特性评价

• 发表时间: 2012
• 作者: 水本将之

LPI法により作製したアルミナ繊維強化複合材料の機械的特性評価

LPI法制备的氧化铝纤维增强复合材料力学性能评价

• 发表时间: 2011
• 作者: Shunsuke Kashiwakura;Yuichi Kumagai;Kazuaki Wagatsuma;平木岳人;水本将之
• 通讯作者: 水本将之

アルミナ繊維・粒子ハイブリッド強化MMCの作製と摩耗特性評価

氧化铝纤维/颗粒混合增强MMC的制备及磨损特性评价

• 发表时间: 2011
• 作者: 平木岳人;長坂徹也;水本将之
• 通讯作者: 水本将之