Semi-capsulation of crack self-healing agents for concrete by introducing granulation technique and strengthening the anti-leakage effect
引入造粒技术，半胶囊化混凝土裂缝自愈剂，增强防渗漏效果
基本信息
- 批准号：23656277
- 负责人：
- 金额：$ 2.66万
- 依托单位：
- 依托单位国家：日本
- 项目类别：Grant-in-Aid for Challenging Exploratory Research
- 财政年份：2011
- 资助国家：日本
- 起止时间：2011 至 无数据
- 项目状态：已结题
- 来源：
- 关键词：
项目摘要
A granulation technology of self-healing agent for crack self-healing concrete, which can repair cracks by itself was developed in order to retain the effect of self-healing agent in long time range. Self-healing agent is granulated by mixing with binder materials. This technology can restrain the contact possibility between self-healing agent and water during mixing and then the fresh property such as slump and flowability of concrete is not affected. Further, the crack self-healing capability can be maintained.
为使裂缝自愈合剂在较长时间内保持其作用效果，研究了一种裂缝自愈合混凝土自愈合剂造粒工艺。自愈剂通过与粘合剂材料混合而成粒。该技术可以抑制自愈合剂在搅拌过程中与水接触的可能性，从而不影响混凝土的坍落度、流动性等新拌性能。此外，可以保持裂纹自愈合能力。
项目成果
期刊论文数量（0）
专著数量（0）
科研奖励数量（0）
会议论文数量（0）
专利数量（0）
造粒によるひび割れ自己治癒性能を有する無機系材料の性能向上に関する基礎研究
造粒提高裂纹自修复无机材料性能的基础研究
- DOI：
- 发表时间：2011
- 期刊：
- 影响因子：0
- 作者：森田卓;小出貴夫;安台浩;岸利治
- 通讯作者：岸利治
{{
item.title }}
{{ item.translation_title }}
- DOI：
{{ item.doi }} - 发表时间：
{{ item.publish_year }} - 期刊：
- 影响因子：{{ item.factor }}
- 作者：
{{ item.authors }} - 通讯作者：
{{ item.author }}
数据更新时间：{{ journalArticles.updateTime }}
{{ item.title }}
- 作者：
{{ item.author }}
数据更新时间：{{ monograph.updateTime }}
{{ item.title }}
- 作者：
{{ item.author }}
数据更新时间：{{ sciAawards.updateTime }}
{{ item.title }}
- 作者：
{{ item.author }}
数据更新时间：{{ conferencePapers.updateTime }}
{{ item.title }}
- 作者：
{{ item.author }}
数据更新时间：{{ patent.updateTime }}
KISHI Toshiharu其他文献
KISHI Toshiharu的其他文献
{{
item.title }}
{{ item.translation_title }}
- DOI：
{{ item.doi }} - 发表时间：
{{ item.publish_year }} - 期刊：
- 影响因子：{{ item.factor }}
- 作者：
{{ item.authors }} - 通讯作者：
{{ item.author }}
{{ truncateString('KISHI Toshiharu', 18)}}的其他基金
A new paradigm for rational maintenance focusing on the effect of water attack and the irrationality of remaining un-carbonated depth as the durability indicator
合理维护的新范式，重点关注水侵蚀的影响和剩余非碳酸化深度作为耐久性指标的不合理性
- 批准号：
19H00778 - 财政年份：2019
- 资助金额：
$ 2.66万 - 项目类别：
Grant-in-Aid for Scientific Research (A)
Generalization of flow regularity of fresh mortar for its implementation to the flow simulation and theoretical extension to rheology
新拌砂浆流动规律的推广，用于流动模拟和流变学理论推广
- 批准号：
16H02354 - 财政年份：2016
- 资助金额：
$ 2.66万 - 项目类别：
Grant-in-Aid for Scientific Research (A)
Development of repeated water drop test for concise total inspection of surface quality of concrete
混凝土表面质量简明全面检测重复落水试验的研制
- 批准号：
25630185 - 财政年份：2013
- 资助金额：
$ 2.66万 - 项目类别：
Grant-in-Aid for Challenging Exploratory Research
VERIFICATION OF COMBINATION USE OF EXPANSIVE AGENT AND LIGHTWEIGHT AGGREGATE ON FATIGUE RESISTANCE OF RC SLAB AND THERMAL STRESS RESTRANT AND ITS UTILIZATION
膨胀剂与轻骨料配合使用对RC板抗疲劳性能及热应力抑制剂的验证及应用
- 批准号：
24656267 - 财政年份：2012
- 资助金额：
$ 2.66万 - 项目类别：
Grant-in-Aid for Challenging Exploratory Research
Prehension of actual quality of cover concrete by field survey and high level integration between durability design and inspection
通过现场调查掌握保护层混凝土的实际质量，耐久性设计与检测的高度结合
- 批准号：
21246069 - 财政年份：2009
- 资助金额：
$ 2.66万 - 项目类别：
Grant-in-Aid for Scientific Research (A)
Mechanism elucidation and constitutive laws of expansive concrete for durable and high performance concrete structures
耐久性高性能混凝土结构膨胀混凝土的机理阐明和本构规律
- 批准号：
13450179 - 财政年份：2001
- 资助金额：
$ 2.66万 - 项目类别：
Grant-in-Aid for Scientific Research (B)
相似海外基金
石灰石骨材コンクリートにおける微細ひび割れの発生制御と高性能化
石灰石骨料混凝土微裂纹控制及性能改善
- 批准号：
23K22835 - 财政年份：2024
- 资助金额：
$ 2.66万 - 项目类别：
Grant-in-Aid for Scientific Research (B)
腐食ひび割れの不均一性を考慮した等価解析モデル開発と実構造物の性能評価への実装
考虑腐蚀裂纹非均匀性的等效分析模型的开发及实际结构性能评估的实施
- 批准号：
24K17337 - 财政年份：2024
- 资助金额：
$ 2.66万 - 项目类别：
Grant-in-Aid for Early-Career Scientists
高炉セメントコンクリートのひび割れ要件解明と水和物形態に基づく収縮抑制手法の開発
阐明高炉水泥混凝土的开裂要求并开发基于水合物形态的收缩抑制方法
- 批准号：
23K26173 - 财政年份：2024
- 资助金额：
$ 2.66万 - 项目类别：
Grant-in-Aid for Scientific Research (B)
ひび割れセンサ機能を有したFRCCの開発
具有裂纹传感器功能的FRCC的开发
- 批准号：
23K04117 - 财政年份：2023
- 资助金额：
$ 2.66万 - 项目类别：
Grant-in-Aid for Scientific Research (C)
高炉セメントコンクリートのひび割れ要件解明と水和物形態に基づく収縮抑制手法の開発
阐明高炉水泥混凝土的开裂要求并开发基于水合物形态的收缩抑制方法
- 批准号：
23H01479 - 财政年份：2023
- 资助金额：
$ 2.66万 - 项目类别：
Grant-in-Aid for Scientific Research (B)
浸水深を考慮したひび割れからの塩化物浸透に関する研究
考虑水浸深度的氯化物裂缝渗透研究
- 批准号：
23K04121 - 财政年份：2023
- 资助金额：
$ 2.66万 - 项目类别：
Grant-in-Aid for Scientific Research (C)
石灰石骨材コンクリートにおける微細ひび割れの発生制御と高性能化
石灰石骨料混凝土微裂纹控制及性能改善
- 批准号：
22H01565 - 财政年份：2022
- 资助金额：
$ 2.66万 - 项目类别：
Grant-in-Aid for Scientific Research (B)
鉄筋コンクリート部材のひび割れ幅の算定精度向上のための付着クリープモデルの開発
开发粘附蠕变模型以提高钢筋混凝土构件裂缝宽度计算的准确性
- 批准号：
22K20450 - 财政年份：2022
- 资助金额：
$ 2.66万 - 项目类别：
Grant-in-Aid for Research Activity Start-up
確率論を導入したマスコンクリートの新たなひび割れ照査方法の提案とその普及
结合概率论的大体积混凝土裂缝验证新方法的提出及其推广
- 批准号：
21K04214 - 财政年份：2021
- 资助金额：
$ 2.66万 - 项目类别：
Grant-in-Aid for Scientific Research (C)
緊張材の能動横拘束で地震損傷RC部材のひび割れを閉合する機動的な応急補強法の開発
开发一种利用主动侧向约束筋束来闭合地震受损钢筋混凝土构件裂缝的移动应急加固方法
- 批准号：
20K04794 - 财政年份：2020
- 资助金额：
$ 2.66万 - 项目类别：
Grant-in-Aid for Scientific Research (C)