Suppression of twin deformation by ordered nano-scale precipitate and its application to room temperature forming

有序纳米级析出物抑制孪晶变形及其在室温成形中的应用

• 批准号: 23656455
• 负责人: KAMADO Shigeharu
• 金额: $ 2.58万
• 依托单位: Nagaoka University of Technology
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Challenging Exploratory Research
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23656455/
• 关键词: マグネシウム合金; 熱間圧延; 動的再結晶; 結晶粒径; 規則GPゾーン; 双晶変形; プレス成形; 機械的性質

Dynamic recrystallization was promoted by high speed rolling at higher temperature and higher reduction ratio and furthermore, dynamic recrystallization with the dynamic precipitation was induced by 1-pass high speed finish rolling at lower temperature and lower reduction ratio, providing the grain size less than 2μm. As a result, the as-rolled sample exhibits almost isotropic and comparable tensile properties with Al alloy used for automotive body panel materials, and a good room temperature bending characteristics after annealing.

当晶粒尺寸小于2μm时，在较高的温度和较高的压下率下进行高速轧制可促进动态再结晶，而在较低的温度和压下率下进行1道次高速精轧机可诱导动态析出的动态再结晶。结果表明，轧制态样品具有与用于汽车车身面板材料的铝合金几乎各向同性和相当的拉伸性能，退火后具有良好的室温弯曲特性。

项目成果

Mg-Al-Ca-Mn系希薄合金のミクロ組織と機械的性質に及ぼす圧延条件の影響

轧制条件对Mg-Al-Ca-Mn稀合金显微组织和力学性能的影响

• 发表时间: 2012
• 作者: 栗原拓也,鎌土重晴

Mg-Al-Ca-Mn合金圧延材のミクロ組織と機械的性質

Mg-Al-Ca-Mn合金轧材的显微组织与力学性能

• 发表时间: 2011
• 作者: 片山翼;田代真一;田中学;上野顕路,徐世偉,本間智之,鎌土重晴
• 通讯作者: 上野顕路,徐世偉,本間智之,鎌土重晴

Mg-Al-Ca-Mn希薄合金のミクロ組織および機械的性質に及ぼす圧延温度の影響

轧制温度对Mg-Al-Ca-Mn稀合金显微组织和力学性能的影响

• 发表时间: 2012
• 作者: 徐世偉;上野顕路;大石敬一郎;鎌土重晴;本間智之
• 通讯作者: 本間智之

Mg-Al-Ca-Mn系希薄合金圧延材のミクロ組織と機械的性質

Mg-Al-Ca-Mn稀合金轧材的显微组织与力学性能

• 发表时间: 2012
• 作者: 栗原拓也;徐世偉;鎌土重晴
• 通讯作者: 鎌土重晴

熱間圧延加工に伴うMg-Al-Ca-Mn合金の動的なミクロ組織変化

Mg-Al-Ca-Mn合金热轧过程中的动态微观结构变化

• 发表时间: 2011
• 作者: 片山翼;田代真一;田中学;上野顕路,徐世偉,本間智之,鎌土重晴;徐 世偉,大石敬一郎,鎌土重晴,本間 智之
• 通讯作者: 徐 世偉,大石敬一郎,鎌土重晴,本間 智之