Evaluation of solidification during welding by in-situ observation and simulation and development of prevention technique for solidification cracking

现场观察模拟焊接凝固评价及凝固裂纹预防技术开发

基本信息

批准号：
24760601
负责人：
KADOI KOTA
金额：
$ 2.58万
依托单位：
Hiroshima University
依托单位国家：
日本
项目类别：
Grant-in-Aid for Young Scientists (B)
财政年份：
2012
资助国家：
日本
起止时间：
2012-04-01 至 2014-03-31
项目状态：
已结题

项目摘要

The aim of this work is for quantitative evaluation of solidification cracking susceptibility during and for investigation of prevention the crack initiation. Evaluation test for hot cracking susceptibility by In-situ observation using high speed camera enabled quantitative measurement the strain and temperature with high accuracy under rapid solidification during laser welding. It was possible to observe distribution morphology of residual liquid at the end of molten pool directly by high magnification in-situ observation technique. In addition, the tendency of the morphology had good agreement with the tendency of the solidification cracking susceptibility.

这项工作的目的是定量评估凝固性裂纹在预防过程中的易感性和调查。使用高速摄像头实现定量测量，通过原位观察进行热开裂敏感性的评估测试，在激光焊接过程中快速固化，应变和温度高精度。可以通过高放大位置观察技术直接观察到熔融池末端的残留液体的分布形态。此外，形态的趋势与固化开裂敏感性的趋势非常吻合。

项目成果

期刊论文数量（0）

专著数量（0）

科研奖励数量（0）

会议论文数量（0）

专利数量（0）

The Effect of Welding Conditions on Solidification Cracking Susceptibility of Type 310S Stainless Steel during Laser Welding Using In-situ Observation Technique

原位观察技术焊接条件对310S不锈钢激光焊接凝固裂纹敏感性的影响

DOI：
发表时间：
期刊：
影响因子：
0
作者：
Tomo Ogura;Taichi Nishida;Hidehito Nishida;Mitsuo Fujimoto and Akio Hirose;Kota Kadoi
通讯作者：
Kota Kadoi

SUS310Sステンレス鋼のレーザ溶接における凝固割れ感受性に及ぼす溶接条件の影響

焊接条件对SUS310S不锈钢激光焊接凝固裂纹敏感性的影响

DOI：
发表时间：
2012
期刊：
影响因子：
0
作者：
Taichi Nishida;Tomo Ogura;Hidehito Nishida;Mitsuo Fujimoto;Makoto Takahashi and Akio Hirose;門井,藤永,山下,山本,篠崎
通讯作者：
門井,藤永,山下,山本,篠崎

The effect of welding conditions on solidification cracking susceptibility of type 310S stainless steel during laser welding using an in-situ observation technique