Functionally graded material designs for application of fusion of cell nuclei

Functionally graded material designs for application of fusion of cell nuclei
用于细胞核融合应用的功能梯度材料设计
批准号:
10044147
负责人:
MIYAHARA Kazuya
金额:
$3.71万
依托单位:
依托单位国家:
日本
项目类别:
Grant-in-Aid for Scientific Research (B).
财政年份:
1998
资助国家:
日本
项目状态:
已结题
起止时间:
1998 至 1999

项目摘要

项目成果

MIYAHARA Kazuya的其他基金

相关文献

中文摘要
翻译
(1) 50% 316-50% W的材料在等离子喷涂后的延展性很低,而316型不锈钢的母材则表现出较大的延展性。(2)拉伸试验用板材试样(厚度1.5mm)在放电加工过程中,热压材料梯度区中心富W区出现断裂,而大块材(厚度约10mm)在放电加工过程中未出现断裂。这被认为是由于加工过程中残余应力的释放。在梯度区外的富W区还观察到较大的裂缝。
英文摘要
(1) The material of the 50% 316-50% W showed very low ductility even just after the fabrication using the plasma spraying method, while the base metal of type 316 stainless steel showed the large ductility.(2) During the discharge machining of plate specimens (thickness : 1.5mm) for tensile test, fracture of W rich zone in the center of graded region of the hot pressed materials occurred, although fracture did not occur during the discharge machining of large block (thickness : about 10mm). This is considered to be due to the release of retained stress during the machining. Another large crack in the W rich zone was observed outside area of the graded region.
期刊论文(0)
专著(0)
科研奖励(0)
会议论文
EFFECT OF ε MARTENSITE ON THE DAMPING PROPERTY OF FE-(CR, AL)-MN SYSTEM ALLOYS
  • 批准号:
    13650757
  • 项目类别:
    Grant-in-Aid for Scientific Research (C)
  • 资助金额:
    $2.24万
  • 财政年份:
    2001
  • 负责人:
    MIYAHARA Kazuya
  • 依托单位:
Effect of oxide species on their particle dispersion behavior and the strength properties of mechanically alloyed ODS ferritic steels
  • 批准号:
    08455333
  • 项目类别:
    Grant-in-Aid for Scientific Research (B)
  • 资助金额:
    $0.96万
  • 财政年份:
    1996
  • 负责人:
    MIYAHARA Kazuya
  • 依托单位:
Fundamental research for the development of new high temperature Fe-Cr-Mn alloys.
  • 批准号:
    03452256
  • 项目类别:
    Grant-in-Aid for General Scientific Research (B)
  • 资助金额:
    $0.58万
  • 财政年份:
    1991
  • 负责人:
    MIYAHARA Kazuya
  • 依托单位: