通过对比染料敏化太阳能电池（DSC）与多晶硅太阳能电池的光电性能发现，短路电流密度偏低是DSC电池光电转换效率不高的重要原因。而DSC电池短路电流密度偏低，主要是由TiO2光阳极过低的电导率明显阻碍了导带电子的快速传递，增加了电子空穴复合产生暗反应的几率引起的。本项目针对DSC电池短路电流密度偏低的问题，拟开发新型超细Al:ZnO/TiO2芯壳纳米电缆光阳极，使外壳与内芯各司其职，即保证TiO2与染料的能级匹配、具有大比表面积（有效吸附单层染料分子），又能显著提高光阳极中电子的传导能力。通过系统研究芯壳电缆内部Al:ZnO纳米线材料电导率以及外壳TiO2膜层厚度等对DSC电池电荷输运机制和光电性能的影响，优化出最佳值，有望使DSC电池的短路电流密度大幅提高，从而显著提高DSC电池的光电转换效率，这为DSC电池新型光阳极的开发提供了新的研究思路，也对促进DSC电池的产业化具有重要意义。

By comparing the photovoltaic performance of dye-sensitized solar cells (DSC) with that of polycrystalline silicon solar cells, it was found that low conversion efficiency of DSSC is mainly due to the low short-circuit photocurrent density. As for DSC, the low conductivity of titania photoanode hinders the rapip charge transfer, increase the recombination rate of electron and hole pair, and thus leads to the low short-circuit photocurrent density. This project intends to develop new ultrafine Al: ZnO/TiO2 core shell nanocable photoanode, makes the outer shell and inner core play their roles, respectively. The band structure of TiO2 shell matches very well to that of dye molecules. Also, titania shell on the ultrafine Al:ZnO nanowire, with large BET surface area, can absorb dye molecules effectively. The conductivity of inner Al:ZnO core is very high, and thus can favor to the rapid charge transfer. We will investigate the effect of conductivity of inner Al:ZnO nanowire and outer titania shell thickness on the charge transfer mechanis and photovoltaic performance. By optimization, short-circuit photocurrent density of DSC is expected to increase obviously, and thus the conversion efficiency will be enhanced markedly, which is significant for developing novel photoanode of DSC and contributing to the industrilization of DSC cells.