Phase composition, microstructure and thermophysical properties of the Srx(Zr0.9Y0.05Yb0.05)O1.95+x ceramics
Phase composition, microstructure and thermophysical properties of the Srx(Zr0.9Y0.05Yb0.05)O1.95+x ceramics
复制标题
Srx(Zr0.9Y0.05Yb0.05)O1.95 x 陶瓷的相组成、显微结构和热物性
DOI：
10.1016/j.jeurceramsoc.2020.12.031
复制
发表时间：
2021-04
期刊：
影响因子：
--
通讯作者：
Manyu Bao
中科院分区：
文献类型：
--
作者：
Wen Ma;Yuanming Gao;Jingxin Zhang;Yu Bai;Ruiling Jia;Hongying Dong;Ruijun Wang;Manyu Bao
采用固相反应烧结法制备了Srx（Zr0.9Y0.05Yb0.05）O1.95+x（x=1.0，0.9，0.8，0.7）陶瓷。烧结的Sr1.0（Zr0.9Y0.05Yb0.05）O2.95是单相固溶体，而烧结的Srx（Zr0.9Y0.05Yb0.05）O1.95+x（x=0.9 - 0.7）是复合物，并且在烧结的Srx（Zr0.9Y0.05Yb0.05）O1.95+x（x=1.0，0.9）中观察到显著的晶粒生长抑制。稀土元素在体相材料中的分布表明，Yb和Y优先取代SrZrO 3中的Zr位，RE 2 O3在纯SrZrO 3中的最高固溶度为10.8mol%。烧结Srx（Zr0.9Y0.05Yb0.05）O1.95+ x的热膨胀系数高达1200°C时的11.0×10− 6 K-1。Sr0.8（Zr0.9Y0.05Yb0.05）O2.75在800°C时的热导率最低，为1.38 W·m-1·K-1。Srx（Zr0.9Y0.05Yb0.05）O1.95+x（x=1.0，0.9，0.8）在600 ~ 1400°C范围内没有相变，而Srx（Zr0.9Y0.05Yb0.05）O1.95+x（x=0.9，0.8）在整个研究温度范围内具有优异的高温相稳定性。因此，Srx（Zr0.9Y0.05Yb0.05）O1.95+x（x=1.0，0.9，0.8）被认为是有前途的热障涂层材料，与YSZ相比，它可以在更高的温度下工作。
Srx(Zr0.9Y0.05Yb0.05)O1.95+x(x=1.0, 0.9, 0.8, 0.7) ceramics were prepared by solid state reaction sintering. The sintered Sr1.0(Zr0.9Y0.05Yb0.05)O2.95is a single-phase solid solution while the sintered Srx(Zr0.9Y0.05Yb0.05)O1.95+x(x=0.9−0.7) are composites, and a significant grain growth inhibition is observed in the sintered Srx(Zr0.9Y0.05Yb0.05)O1.95+x(x=1.0, 0.9). Rare-earth elements distribution in the bulk materials indicates that Yb and Y preferentially substitute Zr-sites in SrZrO3, and the highest solubility of RE2O3in pure SrZrO3is ∼0.8 mol%. The sintered Srx(Zr0.9Y0.05Yb0.05)O1.95+xhave high thermal expansion coefficients up to ∼11.0×10−6K-1(1200°C). Sr0.8(Zr0.9Y0.05Yb0.05)O2.75has the lowest thermal conductivity of 1.38 W·m-1·K-1at 800°C. Srx(Zr0.9Y0.05Yb0.05)O1.95+x(x=1.0, 0.9, 0.8) show no phase transition from 600 to 1400°C, whereas Srx(Zr0.9Y0.05Yb0.05)O1.95+x(x=0.9, 0.8) have excellent high-temperature phase stability over the whole investigated temperature range. Therefore, Srx(Zr0.9Y0.05Yb0.05)O1.95+x (x=1.0, 0.9, 0.8) are considered as promising TBCs materials that might be operated at higher temperatures compared to YSZ.
登录
查看更多内容
影响因子：
3.9
作者：
P. Simoncic;A. Navrotsky
通讯作者：
P. Simoncic;A. Navrotsky
影响因子：
5.7
作者：
Xiaoyu Xie;Hongbo Guo;S. Gong;Huibin Xu
通讯作者：
Xiaoyu Xie;Hongbo Guo;S. Gong;Huibin Xu
DOI：
10.1111/j.1744-7402.2004.tb00182.x
发表时间：
2005-01
影响因子：
2.1
作者：
U. Schulz;B. Saruhan;K. Fritscher;C. Leyens
通讯作者：
U. Schulz;B. Saruhan;K. Fritscher;C. Leyens
影响因子：
3.9
作者：
Wen Ma;D. Mack;R. Vaßen;D. Stöver
通讯作者：
Wen Ma;D. Mack;R. Vaßen;D. Stöver
影响因子：
6.3
作者：
B. Siebert;C. Funke;R. Vaβen;D. Stöver
通讯作者：
B. Siebert;C. Funke;R. Vaβen;D. Stöver