Polyamide-6/Poly(lactic acid) Blends Compatibilized by the Maleic Anhydride Grafted Polyethylene-Octene Elastomer
Polyamide-6/Poly(lactic acid) Blends Compatibilized by the Maleic Anhydride Grafted Polyethylene-Octene Elastomer
复制标题
马来酸酐接枝聚乙烯-辛烯弹性体增容的聚酰胺-6/聚乳酸共混物
DOI：
10.1080/03602559.2010.496418
复制
发表时间：
2010-09
影响因子：
--
通讯作者：
Li, Hai
中科院分区：
文献类型：
--
作者：
Li, Zhong-Ming;Wang, Yu-Ling;Hu, Xiao;Ji, Xu;Li, Hai
为了评价用聚乳酸（PLA）部分取代聚酰胺6（PA 6）的可行性，研究了PA 6/PLA共混体系的形态结构、力学性能和热性能。加入聚乙烯-辛烯弹性体（POE）和POE接枝马来酸酐（POE-g-MAH）以提高共混物的冲击强度和断裂伸长率。结果表明，POE-g-MAH是PA 6/PLA共混体系的有效增容剂。与PA 6/PLA/POE共混体系相比，PA 6/PLA/POE-g-MAH共混体系的粒子尺寸更小，微区分布更均匀，基体与微区之间的界面结合更好。
To evaluate the feasibility of a strategy to partially replace polyamide-6 (PA6) with poly(lactic acid) (PLA), the morphology, mechanical, and thermal properties of PA6/PLA blending systems were investigated. Polyethylene-octene elastomer (POE) and POE grafted with maleic anhydride (POE-g-MAH) are added to improve the impact strength and elongation at break of the blend. The results show that POE-g-MAH is an effective compatibilizer for PA6/PLA blending system. Compared with the morphology of PA6/PLA/POE, smaller particle size, more homogeneous distribution of domains and improved interfacial adhesion between matrix and domains were observed in the PA6/PLA/POE-g-MAH blending system.
登录
查看更多内容
影响因子：
3
作者：
Hongyuan Cheng;M. Tian;Liqun Zhang
通讯作者：
Hongyuan Cheng;M. Tian;Liqun Zhang
DOI：
10.1002/(sici)1439-2054(20000301)276:1
发表时间：
2000-03
影响因子：
3.9
作者：
E. Meyer;H. Braun
通讯作者：
E. Meyer;H. Braun
影响因子：
3
作者：
S. López-Quintana;C. Rosales;I. Gobernado-Mitre;J. Merino;J. M. Pastor
通讯作者：
S. López-Quintana;C. Rosales;I. Gobernado-Mitre;J. Merino;J. M. Pastor
影响因子：
2.1
作者：
S. Bai;Ke Cao;Jian-kang Chen;Z. Liu
通讯作者：
S. Bai;Ke Cao;Jian-kang Chen;Z. Liu
影响因子：
4.5
作者：
Hong-yan Tian;H. Tagaya
通讯作者：
Hong-yan Tian;H. Tagaya